Stress corrosion cracking failure of friction stir welded nuclear grade austenitic stainless steel
Engineering Failure Analysis
◽
10.1016/j.engfailanal.2020.105012
◽
2021
◽
Vol 120
◽
pp. 105012
Author(s):
R. Rajasekaran
◽
A.K. Lakshminarayanan
◽
R. Damodaram
◽
V. Balasubramanian
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Corrosion Cracking
◽
Nuclear Grade
◽
Friction Stir
Download Full-text
Related Documents
Cited By
References
Analysis of the early stage of stress corrosion cracking in austenitic stainless steel by EBSD and XRD
Materials Characterization
◽
10.1016/j.matchar.2021.110882
◽
2021
◽
pp. 110882
Author(s):
Tomoyuki Fujii
◽
Ryohei Yamakawa
◽
Keiichiro Tohgo
◽
Yoshinobu Shimamura
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Early Stage
◽
Corrosion Cracking
Download Full-text
The influence of chloride content, pH and temperature of test solution on the occurrence of stress corrosion cracking with austenitic stainless steel
Corrosion Science
◽
10.1016/0010-938x(77)90069-5
◽
1977
◽
Vol 17
(9)
◽
pp. 737-746
◽
Cited By ~ 47
Author(s):
J.E. Truman
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Chloride Content
◽
Corrosion Cracking
◽
Test Solution
Download Full-text
Stress—corrosion cracking of austenitic stainless steel in hydrochloric acid media at room temperature
Corrosion Science
◽
10.1016/0010-938x(73)90012-7
◽
1973
◽
Vol 13
(3)
◽
pp. 165-173
◽
Cited By ~ 40
Author(s):
G. Bianchi
◽
F. Mazza
◽
S. Torchio
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Hydrochloric Acid
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Room Temperature
◽
Corrosion Cracking
◽
Acid Media
◽
Hydrochloric Acid Media
Download Full-text
Toward Understanding the Effects of Strain and Chloride Deposition Density on Atmospheric Chloride-Induced Stress Corrosion Cracking of Type 304 Austenitic Stainless Steel Under MgCl2 and FeCl3:MgCl2 Droplets
CORROSION
◽
10.5006/3026
◽
2018
◽
Vol 75
(2)
◽
pp. 167-182
◽
Cited By ~ 10
Author(s):
C. Örnek
◽
D.L. Engelberg
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Corrosion Cracking
◽
Induced Stress
◽
Deposition Density
◽
304 Austenitic Stainless Steel
◽
Chloride Deposition
◽
Type 304
Download Full-text
Effect of low-temperature surface carburization on stress corrosion cracking of AISI 304 austenitic stainless steel
Surface and Coatings Technology
◽
10.1016/j.surfcoat.2017.08.058
◽
2017
◽
Vol 328
◽
pp. 420-427
◽
Cited By ~ 18
Author(s):
Yawei Peng
◽
Chaoming Chen
◽
Xuanyi Li
◽
Jianming Gong
◽
Yong Jiang
◽
...
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Low Temperature
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Corrosion Cracking
◽
Aisi 304
◽
304 Austenitic Stainless Steel
◽
Temperature Surface
Download Full-text
Electrochemical noise measurements of stress corrosion cracking of sensitised austenitic stainless steel in high-purity oxygenated water at 288°C
Corrosion Science
◽
10.1016/0010-938x(92)90018-x
◽
1992
◽
Vol 33
(1)
◽
pp. 73-88
◽
Cited By ~ 50
Author(s):
J. Stewart
◽
D.B. Wells
◽
P.M. Scott
◽
D.E. Williams
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
High Purity
◽
Electrochemical Noise
◽
Corrosion Cracking
◽
Noise Measurements
◽
Oxygenated Water
Download Full-text
Stress Corrosion Cracking and Hydrogen-Induced Cracking in Austenitic Stainless Steel under Mode II Loading
CORROSION
◽
10.5006/1.3582025
◽
1988
◽
Vol 44
(1)
◽
pp. 50-55
◽
Cited By ~ 16
Author(s):
L.-J. Qiao
◽
W.-Y. Chu
◽
C.-M. Hsiao
◽
J.-D. Lu
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Corrosion Cracking
◽
Mode Ii
◽
Hydrogen Induced Cracking
◽
Mode Ii Loading
Download Full-text
Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions
Materials
◽
10.3390/ma7127799
◽
2014
◽
Vol 7
(12)
◽
pp. 7799-7808
◽
Cited By ~ 12
Author(s):
R. Raman
◽
Wai Siew
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Corrosion Cracking
◽
Chloride Solutions
Download Full-text
Stress Corrosion Cracking on an Insulated Austenitic Stainless Steel Pressure Vessel
10.2118/186287-ms
◽
2017
◽
Author(s):
Padang Wikar Hapsoro
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Pressure Vessel
◽
Corrosion Cracking
Download Full-text
Stress corrosion cracking of austenitic stainless steel Type 316 in acid solutions and intergranular SCC mechanism: effects of anion species (Cl− and SO4−2− and sensitizing temperature
Environment-Induced Cracking of Materials
◽
10.1016/b978-008044635-6.50040-6
◽
2008
◽
pp. 419-433
Author(s):
R. Nishimura
◽
A. Sulaiman
◽
Y. Maeda
Keyword(s):
Stainless Steel
◽
Austenitic Stainless Steel
◽
Stress Corrosion
◽
Stress Corrosion Cracking
◽
Corrosion Cracking
◽
Acid Solutions
◽
Steel Type
◽
Anion Species
Download Full-text
Sign in / Sign up
Close
Export Citation Format
Close
Share Document
Close