A series of polycrystalline (Ca1-xBix)3Co4O9 ( x = 0.0 ~ 0.075 ) powders were synthesized rapidly by a polyacrylamide gel method. The dense ceramics were fabricated using the spark plasma sintering ( SPS ) technique. Effects of Bi substitution on high temperature thermoelectric properties of Ca3Co4O9 were evaluated. Both the electrical conductivity and Seebeck coefficient increased with increasing Bi content up to x = 0.05, thus leading to an enhanced thermoelectric power factor. The Bi substituted sample with x = 0.05 obtained in this study has the highest thermoelectric power factor in the measured temperature range. It reaches 4.810-4 Wm-1K-2 at 700 °C, which is 26 % higher than that of Ca3Co4O9 without Bi substitution, and is by up to 15 % larger as compared to the Bi substituted sample synthesized by the solid state reaction method and the SPS technique due to the high chemical homogeneous powder prepared by the polyacrylamide gel method.
High sintering activity NaNbO3 powder synthesis via the polyacrylamide gel method and fabrication of a NaNbO3 ceramic at lower temperature