Effect of hydrogen on the stress corrosion cracking behavior of X80 pipeline steel in Ku'erle soil simulated solution

2009 ◽  
Vol 16 (4) ◽  
pp. 407-413 ◽  
Author(s):  
Ping Liang ◽  
Cui-wei Du ◽  
Xiao-gang Li ◽  
Xu Chen ◽  
Zhang liang
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Pipeline Steel ◽  
Corrosion Cracking ◽  
X80 Pipeline Steel ◽  
Cracking Behavior

scholarly journals Influence of the ultrasonic surface rolling process on stress corrosion cracking susceptibility of high strength pipeline steel in neutral pH environment

RSC Advances ◽  
2017 ◽  
Vol 7 (59) ◽  
pp. 36876-36885 ◽  
Author(s):  
Bingying Wang ◽  
Yu Yin ◽  
Zhiwei Gao ◽  
Zhenbo Hou ◽  
Wenchun Jiang
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Pipeline Steel ◽  
High Strength ◽  
Rolling Process ◽  
Corrosion Cracking ◽  
X80 Pipeline Steel ◽  
Enhancement Technique ◽  
Neutral Ph ◽  
Developed Surface

A developed surface enhancement technique, USRP, was applied on X80 pipeline steel and the stress corrosion cracking susceptibility was studied.