Sulfoaluminate cement (SAC) was utilized for the solidification/stabilization of fly ash from municipal solid waste (MSW) incinerators. The effects of fly ash amount and water/binder ratio were investigated on compressive strength and heavy metals leaching toxicity of solidified matrices at different curing times. The results showed that prolonged curing time, lower fly ash amount and water/binder ratio enhanced the compressive strength and decreased the leaching concentrations of Zn, Pb and Cu. For 28 days cured matrices with fly ash amount 50% and water/binder ratio 0.30, the compressive strength was 32.6 MPa and the leaching concentrations of Zn, Pb and Cu were 14.73, 0.75 and 0.43 mg/L respectively. The leaching concentrations of Zn, Pb and Cu met the demand of GB 5085.3-2007. SAC is proved to be effective for MSW incinerator fly ash solidification/stabilization and high performance matrices for disposal and reuse may be achieved with further formula optimization.
Associations between oxidative stress levels and total duration of engagement in jobs with exposure to fly ash among workers at municipal solid waste incinerators