scholarly journals Calcium carbonate modified urea–formaldehyde resin adhesive for strength enhanced medium density fiberboard production

RSC Advances ◽  
2021 ◽  
Vol 11 (40) ◽  
pp. 25010-25017
Author(s):  
Li Lu ◽  
Yan Wang ◽  
Tianhua Li ◽  
Supeng Wang ◽  
Shoulu Yang ◽  
...  
Keyword(s):  
Calcium Carbonate ◽  
Urea Formaldehyde ◽  
Medium Density Fiberboard ◽  
Urea Formaldehyde Resin ◽  
Formaldehyde Resin ◽  
Medium Density ◽  
Ionic Bond ◽  
Resin Adhesive ◽  
Uf Resin ◽  
Modified Urea

Reactions between CaCO3 and CH2O2 during polycondensation of UF resin produce Ca2+. Ionic bond complexation binds Ca2+ with UF resin. The UF resin crystalline percentage decreases from 26.86% to 22.71%. IB strength of resin bonded fiberboard increases from 0.75 to 0.94 MPa.

Easy procedure to prepare nitrogen-containing activated carbons for supercapacitors

RSC Advances ◽  
2014 ◽  
Vol 4 (73) ◽  
pp. 39037-39044 ◽  
Author(s):  
Tong-Xin Shang ◽  
Ming-Yang Zhang ◽  
Xiao-Juan Jin
Keyword(s):  
Activated Carbons ◽  
Urea Formaldehyde ◽  
Medium Density Fiberboard ◽  
Urea Formaldehyde Resin ◽  
Formaldehyde Resin ◽  
Medium Density ◽  
Resin Adhesive

The urea-formaldehyde resin adhesive in waste medium density fiberboard play a role in modifying the activated carbons.

Labile Extractable Urea-Formaldehyde Resin Components from Medium-Density Fiberboard*

2015 ◽  
Vol 65 (1-2) ◽  
pp. 15-19 ◽  
Author(s):  
Warren J. Grigsby ◽  
James E. P. Carpenter ◽  
Armin Thumm ◽  
Rosie Sargent ◽  
Nancy Hati
Keyword(s):  
Urea Formaldehyde ◽  
Medium Density Fiberboard ◽  
Urea Formaldehyde Resin ◽  
Formaldehyde Resin ◽  
Medium Density

The Impact of Different Dosage of Additives on the UF Resin Used in Plywood

2011 ◽  
Vol 197-198 ◽  
pp. 147-150 ◽  
Author(s):  
Wei Wang ◽  
Li Bin Zhu ◽  
Ji You Gu ◽  
Xiang Li Weng ◽  
Hai Yan Tan
Keyword(s):  
Urea Formaldehyde ◽  
Formaldehyde Emission ◽  
Urea Formaldehyde Resin ◽  
Formaldehyde Resin ◽  
Synthetic Process ◽  
Resin Adhesive ◽  
Environmental Friendly ◽  
Uf Resin ◽  
Comprehensive Performance ◽  
The Impact

Through the study of the effects of different dosage of additives on the properties of urea formaldehyde resin adhesive prepared at low mole ratio of formaldehyde/urea, optimize the synthetic process of the UF resin which is used at the E0 grade plywood. The results showed that the product synthesized under the following condition: the mole ratio of formaldehyde/urea is 0.99:1, the dosage of the specific additive is 1.0% and that of melamine is 3-4%, had a good comprehensive performance and the formaldehyde emission of the plywood meets the E0 grade which is environmental-friendly.

Performances of Modified Urea-Formaldehyde Resins for Bonding Plywood

2011 ◽  
Vol 71-78 ◽  
pp. 3170-3173
Author(s):  
Ji Zhi Zhang ◽  
Xiao Ying Liu ◽  
Ying Ying Qiu ◽  
Xiao Mei Wang ◽  
Jian Zhang Li ◽  
...  
Keyword(s):  
Urea Formaldehyde ◽  
Formaldehyde Emission ◽  
Exothermic Peak ◽  
Urea Formaldehyde Resin ◽  
Molar Ratio ◽  
Formaldehyde Resin ◽  
Formaldehyde Content ◽  
Uf Resin ◽  
Dta Curve ◽  
Modified Urea

Urea-formaldehyde resin was modified by a modifier with different synthetic processes labelled as UFM1, UFM2, and UFM3 respectively. As a comparison, normal UF resin with a F/U molar ratio of 1.1 labelled as UF0 was synthesized. The thermal behavior of modified urea-formaldehyde resins was studied by TG-DTA techniques, and the properties of plywood bonded with the UFM resins were investigated. The conclusions were as follows: (1) the modifier used in this study could significantly reduce the free formaldehyde content of urea-formaldehyde resin and the formaldehyde emission of plywood; (2) The exothermic peak temperatures of DTA curve were 129.37, 125.05, 120.98, and 116.11 °C for UF0, UFM1, UFM2, and UFM3 respectively. (3) The plywood manufactured with UFM2 and UFM3 resins have high bonding strength (1.28MPa and 1.59MPa) and low formaldehyde emission value (E1 grade).

Study on Urea-Formaldehyde Resin for Glass Wool Products

2013 ◽  
Vol 774-776 ◽  
pp. 1232-1236
Author(s):  
Nan Zhe Zhang
Keyword(s):  
Polyvinyl Alcohol ◽  
Water Resistance ◽  
Urea Formaldehyde ◽  
Glass Wool ◽  
Orthogonal Test ◽  
Urea Formaldehyde Resin ◽  
Molar Ratio ◽  
Formaldehyde Resin ◽  
Resin Adhesive ◽  
Uf Resin

In order to prepare urea-formaldehyde (UF) resin adhesive with good performance for glass wool products, we used polyvinyl alcohol (PVA), p-toluenesulfonamide (PTSA) and methanol to modify UF resin, optimized the molar ratio of formaldehyde (F) / urea (U) and reaction components ratio by orthogonal test, reduced the content of free formaldehyde in UF resin, and enhanced the water resistance, flexibility and stability of UF resin.

Sign in / Sign up

Export Citation Format

Share Document