scholarly journals Deformation and Residual Stress Characteristics of TC17 Alloy Subjected to Laser Shock Peening with Single and Double Sides

2019 ◽  
Vol 493 ◽  
pp. 012001
Author(s):  
Minghuang Zhao ◽  
Chenghong Duan ◽  
Jiayi Li ◽  
Xiangpeng Luo
Keyword(s):  
Residual Stress ◽  
Laser Shock Peening ◽  
Laser Shock ◽  
Shock Peening

Fatigue Life Recovery via Laser Shock Peening in Mechanically Damaged Aluminium Sheet; Experiments and Prediction Models

2014 ◽  
Vol 891-892 ◽  
pp. 980-985 ◽  
Author(s):  
Niall Smyth ◽  
Philip E. Irving
Keyword(s):  
Residual Stress ◽  
Fatigue Life ◽  
Prediction Models ◽  
Load Cycle ◽  
Laser Shock Peening ◽  
Stress Fields ◽  
Hole Drilling ◽  
Laser Shock ◽  
Aluminium Sheet ◽  
Shock Peening

This paper reports the effectiveness of residual stress fields induced by laser shock peening (LSP) to recover pristine fatigue life. Scratches 50 and 150 μm deep with 5 μm root radii were introduced into samples of 2024-T351 aluminium sheet 2 mm thick using a diamond tipped tool. LSP was applied along the scratch in a band 5 mm wide. Residual stress fields induced were measured using incremental hole drilling. Compressive residual stress at the surface was-78 MPa increasing to-204 MPa at a depth of 220 μm. Fatigue tests were performed on peened, unpeened, pristine and scribed samples. Scratches reduced fatigue lives by factors up to 22 and LSP restored 74% of pristine life. Unpeened samples fractured at the scratches however peened samples did not fracture at the scratches but instead on the untreated rear face of the samples. Crack initiation still occurred at the root of the scribes on or close to the first load cycle in both peened and unpeened samples. In peened samples the crack at the root of the scribe did not progress to failure, suggesting that residual stress did not affect initiation behaviour but instead FCGR. A residual stress model is presented to predict crack behaviour in peened samples.

Massive Parallel Laser Shock Peening: Simulation, Verification, and Analysis

2005 ◽  
Author(s):  
A. W. Warren ◽  
Y. B. Guo ◽  
S. C. Chen
Keyword(s):  
Residual Stress ◽  
Surface Integrity ◽  
Compressive Residual Stress ◽  
Laser Intensity ◽  
Shock Pressure ◽  
Laser Shock Peening ◽  
Massively Parallel ◽  
Laser Shock ◽  
Laser Material ◽  
Shock Peening

Laser shock peening (LSP) is a surface treatment process to improve the surface integrity of metallic components. The nearly pure mechanical process of LSP results in favorable surface integrity such as compressive residual stress and improved surface material properties. Since LSP is a transient process with laser pulse duration time on the order of 40 ns, real time in-situ measurement of laser/material interaction is very challenging, if not impossible. A fundamental understanding of laser/material interactions is essential for LSP planning. Previous finite element simulations of LSP have been limited to a single laser shock location for both two and three dimensional modeling. However, actual LSP are performed in a massively parallel mode which involves almost simultaneous multi-laser/material interactions in order to induce uniform compressive residual stress across the entire surface of the workpiece. The massively parallel laser/material interactions have a significant compound/interfering effect on the resulting surface integrity of the workpiece. The numerical simulation of shock pressure as a function of time and space during LSP is another critical problem. The purpose of this paper is to investigate the effects of parallel multiple laser/material interactions on the stress/strain distributions in the workpiece during LSP of AISI 52100 steel. FEA simulations of LSP in single and multiple passes were performed with the developed spatial and temporal shock pressure model via a subroutine. The simulated residual stresses agree with the measured data in nature and trend, while magnitude can be influenced by the interactions between neighboring peening zones and the locations of residual stress measurement. Design-of-experiment (DOE) based simulations of massive parallel LSP were also performed to determine the effects of laser intensity, laser spot size, and peening spacing on stresses and strains. Increasing the laser intensity increases both the stress magnitude and affected depth. The use of smaller laser spot sizes decreases the largest magnitude of residual stress and also decreases the depth affected by LSP. Larger spot sizes have less energy attenuation and cause more plastic deformation. Spacing between peening zones is critical for the uniformity of mechanical properties across the surface. The greatest uniformity and largest stress magnitudes are achieved by overlapping of the laser spots.

scholarly journals Improvement of Fatigue Life of GH3039 Superalloy by Laser Shock Peening

Materials ◽  
2020 ◽  
Vol 13 (17) ◽  
pp. 3849
Author(s):  
Yang Tang ◽  
MaoZhong Ge ◽  
Yongkang Zhang ◽  
Taiming Wang ◽  
Wen Zhou
Keyword(s):  
Residual Stress ◽  
Fatigue Life ◽  
Surface Profile ◽  
Optical Microscope ◽  
Laser Shock Peening ◽  
Laser Shock ◽  
Transmission Electron ◽  
Before And After ◽  
Shock Peening ◽  
Improve Fatigue

In order to improve fatigue life of GH3039 superalloy, GH3039 superalloy sheets were treated by laser shock peening (LSP). The microstructure of GH3039 superalloy before and after LSP was characterized using an optical microscope, transmission electron microscope (TEM), and X-ray diffractometer. The fatigue life of the samples with and without LSP was investigated by fatigue experiments. Moreover, surface profile and residual stress were also examined. Experimental results indicated that the grains in the surface layer of the LSP sample were remarkably refined and reached the nanometer scale. The average surface roughness increased from 0.024 μm to 0.19 μm after LSP. The average fatigue life of the laser treated samples was 2.01 times larger than that of the untreated specimens. Additionally, mathematical statistical analysis confirms that LSP has a significant influence on the fatigue life of GH3039 superalloy. The improvement of fatigue life for the laser processed GH3039 superalloy was mainly attributed to compressive residual stress and grain refinement generated by LSP.

Numerical Investigation of Opposing Dual Sided Micro Scale Laser Shock Peening

2006 ◽  
Author(s):  
Yajun Fan ◽  
Youneng Wang ◽  
Sinisa Vukelic ◽  
Y. Lawrence Yao
Keyword(s):  
Residual Stress ◽  
Shock Waves ◽  
Laser Shock Peening ◽  
Time Lags ◽  
Laser Shock ◽  
Surface Residual Stress ◽  
Strain Rate Effects ◽  
Micro Scale ◽  
Stress Profiles ◽  
Shock Peening

Laser shock peening (LSP) is an innovative process which imparts compressive residual stresses in the processed surface of metallic parts to significantly improve fatigue life and fatigue strength of this part. In opposing dual sided LSP, the workpiece can be simultaneously irradiated or irradiated with different time lags to create different surface residual stress patterns by virtue of the interaction between the opposing shock waves. In this work, a finite element model, in which the hydrodynamic behavior of the material and the deviatoric behavior including work hardening and strain rate effects were considered was applied to predict residual stress distributions in the processed surface induced under various conditions of the opposing dual sided micro scale laser shock peening. Thus the shock waves from each surface will interact in different ways through the thickness resulting in more complex residual stress profiles. Additionally, when treating a thin section, opposing dual sided peening is expected to avoid harmful effects such as spalling and fracture because the pressures on the opposite surfaces of the target balance one another and prohibit excessive deformation of the target. In order to better understand the wave-wave interactions under different conditions, the residual stress profiles corresponding to various workpiece thicknesses and various irradiation times were evaluated.