Microstructure and Mechanical properties of transition zone in laser additive manufacturing of TC4/AlSi12 bimetal structure

Ti/Al bimetallic structure (BS) has a good development prospect and broader application potential in aerospace engineering. Considering the limitation that dissimilar welding is only applicable to the thin plate, it is necessary to explore a new manufacturing process for Ti/Al BS. In this study, a TC4/AlSi12 BS was prepared by laser additive manufacturing (LAM). TC4 zone, AlSi12 zone and transition zone were formed in the LAM process. Due to the sufficient diffusion reaction, the transition zone with a width of about 0.8mm was obtained. At the same time, a few micro-cracks were found in the transition zone. The microstructure and phase composition of the transition zone had been emphatically studied. Research results showed that the presence of Si element made the phase composition of the transition zone more complicated. The structure evolution from TC4 to AlSi12 was: α-Ti → Ti3Al → TiAl+(TiAl+Si) → Ti5Si3 → TiAl3+(α-Al+Si) → α-Al+ Si +TiAl3 +(α-Al+Si) → α-Al+Si+(α-Al+Si). The hardness distribution of BS was uneven, with the highest value reaching 524HV. The tensile strength of the TC4/AlSi12 BS was about 110Mpa, and the fracture location was located in the transition zone.