Fracture toughness is a material property in the same sense that yield strength is a material property. The determination of fracture toughness for dynamic loading conditions is not very straightforward, as dynamic crack growth speed in supersonic speed and the speed range is 1 to 2 km/sec. The improvement of fracture toughness of metals plays a vital role in the design and manufacturing of structural components. To achieve this purpose, industries rely up on coatings which are an integral part of manufacturing. These coated samples are tested by Charpy V-notch impact testing for estimating dynamic fracture toughness. These coatings improve the wear and corrosion resistance of the materials and they tend to reduce the strength of the materials, because of the increased residual stresses due to the coating process. These defects cannot be precluded from these coated and treated components. The strength of those components in the presence of such defects can be analyzed by fracture mechanics approach. An attempt has been made to analyze the effect of coating methods like electroplating and PVD (Physical Vapour Deposition), coating thickness, heat treatment and the service temperature on the fracture behavior of metals. The experiments have been carried out on EN8 steel and aluminium for different temperatures. The specimen preparation and experimentations were carried out according to the ASTM standard E-23. The FRANC 2D (Fracture Analysis Code) has been relied upon for estimating the stress intensity factor at different crack length and temperature.
Measurement of Dynamic Fracture Toughness of 13% Cr Cast Stainless Steel by Instrumented Charpy Test