Spin Echo Self-Diffusion Measurements in Molten Salts

1988 ◽  
Vol 43 (12) ◽  
pp. 1075-1082 ◽  
Author(s):  
C. Herdlicka ◽  
J. Richter ◽  
M. D. Zeidler
Keyword(s):  
Magnetic Field ◽  
Diffusion Coefficients ◽  
Molten Salts ◽  
Spin Echo ◽  
Pulsed Magnetic Field ◽  
Self Diffusion ◽  
Field Gradients ◽  
Magnetic Field Gradients ◽  
Spin Echo Technique ◽  
Probe Head

An NMR probe head for diffusion measurements in molten salts at temperatures up to 673 K is described. The spin echo technique using pulsed magnetic field gradients was employed. Resulting self-diffusion coefficients of Na+ in molten NaNO3 in the temperature range 596-670 K are compa­red with literature data obtained by other methods.

Temperature and Pressure Dependence of Self Diffusion in Octamethylcyclotetrasiloxane and Hexamethylcyclotrisilazane

1990 ◽  
Vol 45 (11-12) ◽  
pp. 1281-1284 ◽  
Author(s):  
A. Greiner-Schmid ◽  
M. Has ◽  
H.-D. Lüdemann
Keyword(s):  
Magnetic Field ◽  
Pressure Dependence ◽  
Spin Echo ◽  
The Self ◽  
Self Diffusion ◽  
Field Gradients ◽  
Magnetic Field Gradients ◽  
Temperature And Pressure ◽  
Spin Echo Technique ◽  
Self Diffusion Coefficient

AbstractThe pressure dependence of the self diffusion coefficient D for octamethylcyclotetrasiloxane and hexamethylcyclotrisilazane has been determined by the NMR spin echo technique with pulsed magnetic field gradients at pressures up to 200 MPa and at temperatures between 490 K and 290 K. The data extend partially into the deeply supercooled range. The isobaric temperature dependence of these data is quantitatively described by the empirical Vogel-Fulcher-Tammann equation. For both substances the melting pressure curves were determined in addition.

Self-Diffusion in Molten Lithium Nitrate

1992 ◽  
Vol 47 (10) ◽  
pp. 1047-1050 ◽  
Author(s):  
C. Herdlicka ◽  
J. Richter ◽  
M. D. Zeidler
Keyword(s):  
Diffusion Coefficient ◽  
Diffusion Coefficients ◽  
Spin Echo ◽  
The Self ◽  
Lithium Nitrate ◽  
Equimolar Ratio ◽  
Self Diffusion ◽  
Field Gradients ◽  
Molten Lithium ◽  
Self Diffusion Coefficient

AbstractSelf-diffusion coefficients of 7Li+ ions have been measured in molten LiNO3 with several compositions of 6Li+ and 7Li+ over a temperature range from 537 to 615 K. The NMR spin-echo method with pulsed field gradients was applied. It was found that the self-diffusion coefficient depends on the isotopic composition and shows a maximum at equimolar ratio. At temperatures above 600 K this behaviour disappears.

NMR Microscopy Using Large, Pulsed Magnetic-Field Gradients

1995 ◽  
Vol 108 (2) ◽  
pp. 125-136 ◽  
Author(s):  
C.J. Rofe ◽  
J. Vannoort ◽  
P.J. Back ◽  
P.T. Callaghan
Keyword(s):  
Magnetic Field ◽  
Pulsed Magnetic Field ◽  
Nmr Microscopy ◽  
Field Gradients ◽  
Magnetic Field Gradients
Sign in / Sign up

Export Citation Format

Share Document