Photoluminescence Characteristics of Sn2+ and Ce3+-Doped Cs2SnCl6 Double-Perovskite Crystals

In recent years, all-inorganic lead-halide perovskites have received extensive attention due to their many advantages, but their poor stability and high toxicity are two major problems. In this paper, a low toxicity and stable Cs2SnCl6 double perovskite crystals were prepared by aqueous phase precipitation method using SnCl2 as precursor. By the XRD, ICP-AES, XPS, photoluminescence and absorption spectra, the fluorescence decay curve, the structure and photoluminescence characteristics of Ce3+-doped and undoped samples have been investigated in detail. The results show that the photoluminescence originates from defects. [ S n S n 4 + 2 + +VCl] defect complex in the crystal is formed by Sn2+ substituting Sn4+. The number of defects formed by Sn2+ in the crystal decreases with Ce3+ content increases. Within a certain number of defects, the crystal luminescence is enhanced with the number of [ S n S n 4 + 2 + +VCl] decreased. When Ce3+ is incorporated into the crystals, the defects of [ C e 3 + S n 4 + +VCl] and [ S n S n 4 + 2 + +VCl] were formed and the crystal show the strongest emission. This provides a route to enhance the photoluminescence of Cs2SnCl6 double perovskite crystals.