scholarly journals Impact of Iron on the Fe–Co–Ni Ternary Nanocomposites Structural and Magnetic Features Obtained via Chemical Precipitation Followed by Reduction Process for Various Magnetically Coupled Devices Applications

Nanomaterials ◽  
2021 ◽  
Vol 11 (2) ◽  
pp. 341
Author(s):  
Tien Hiep Nguyen ◽  
Gopalu Karunakaran ◽  
Yu.V. Konyukhov ◽  
Nguyen Van Minh ◽  
D.Yu. Karpenkov ◽  
...  

This paper presents the synthesis of Fe–Co–Ni nanocomposites by chemical precipitation, followed by a reduction process. It was found that the influence of the chemical composition and reduction temperature greatly alters the phase formation, its structures, particle size distribution, and magnetic properties of Fe–Co–Ni nanocomposites. The initial hydroxides of Fe–Co–Ni combinations were prepared by the co-precipitation method from nitrate precursors and precipitated using alkali. The reduction process was carried out by hydrogen in the temperature range of 300–500 °C under isothermal conditions. The nanocomposites had metallic and intermetallic phases with different lattice parameter values due to the increase in Fe content. In this paper, we showed that the values of the magnetic parameters of nanocomposites can be controlled in the ranges of MS = 7.6–192.5 Am2/kg, Mr = 0.4–39.7 Am2/kg, Mr/Ms = 0.02–0.32, and HcM = 4.72–60.68 kA/m by regulating the composition and reduction temperature of the Fe–Co–Ni composites. Due to the reduction process, drastic variations in the magnetic features result from the intermetallic and metallic face formation. The variation in magnetic characteristics is guided by the reduction degree, particle size growth, and crystallinity enhancement. Moreover, the reduction of the surface spins fraction of the nanocomposites under their growth induced an increase in the saturation magnetization. This is the first report where the influence of Fe content on the Fe–Co–Ni ternary system phase content and magnetic properties was evaluated. The Fe–Co–Ni ternary nanocomposites obtained by co-precipitation, followed by the hydrogen reduction led to the formation of better magnetic materials for various magnetically coupled device applications.

2010 ◽  
Vol 152-153 ◽  
pp. 1044-1048
Author(s):  
Lai Qiang Li ◽  
Shu Lin Wang ◽  
Jie Liu ◽  
Sheng Juan Li ◽  
Jun Jing Zhang

The nanoparticles of Fe3O4 were prepared with chemical precipitation method, and then used sodium oleate and the lauryl sulfonic aid sodium as bilayer to envelope the ultra-fine Fe3O4 particles. Then stabilized water base magnetic fluid was obtained. The crystallization behavior and the surface of Fe3O4 nanoparticles after the modification were investigated with XRD and IR respectively; the particle size was studied with TEM; the magnetic properties were studied with VSM. The mechanism of bilayer surfactants that modified Fe3O4 magnetic nanoparticles was explained, and influencing factors of the magnetic fluid were discussed.


2018 ◽  
Vol 44 (17) ◽  
pp. 20782-20789 ◽  
Author(s):  
Rohit R. Powar ◽  
Varsha D. Phadtare ◽  
Vinayak G. Parale ◽  
Hyung-Ho Park ◽  
Sachin Pathak ◽  
...  

2018 ◽  
Vol 281 ◽  
pp. 40-45
Author(s):  
Jie Guang Song ◽  
Lin Chen ◽  
Cai Liang Pang ◽  
Jia Zhang ◽  
Xian Zhong Wang ◽  
...  

YAG materials has a number of unique properties, the application is very extensive. In this paper, the superfine YAG powder materials were prepared by co-precipitation method and hydrothermal precipitation method. The influence of synthesis process on the morphology of the powder was investigated. The results showed that the precursor powder prepared via the co-precipitation method is mainly from amorphous to crystalline transition with the increasing calcination temperature, the precursor agglomeration is more serious, In the process of increasing the calcination temperature, the dispersibility of the roasted powder is greatly improved, which is favorable for the growth of the crystal grains, so that the particle size of the powder is gradually increased, the YAG precursor prepared by the co-precipitation method is transformed into YAG crystals, the phase transition occurs mainly between 900 and 1100°C. When the molar ratio of salt to alkali is Y3+: OH-=1: 8 via the hydrothermal reaction, the YAG particles with homogeneous morphology can be obtained. When the molar ratio of salt and alkali is increased continuously, the morphology of YAG particles is not obviously changed. The co-precipitation method is easy to control the particle size, the hydrothermal method is easy to control the particle morphology.


2018 ◽  
Vol 56 (1) ◽  
pp. 31
Author(s):  
Luong Thi Quynh Anh ◽  
Nguyen Van Dan ◽  
Do Minh Nghiep

The crystalline nanoparticles of Ni0.2Zn0.8Fe2O4 ferrite were synthesized by chemical co-precipitation with precursor concentration of 0.1M, then modified by 0.25M solution of oleic acid in pentanol, finally heated at temperatures 120, 140, 160 and 180oC for 6h in autoclave. The XRD, EDS and TEM confirmed that all of samples are crystalline and their particle size are 6, 6.5, 7 and 8 nm. The magnetic properties showed that the coercive force, the remanence of samples are about zero, the saturation magnetization Ms has values from 14.20 to 27.12 emu/g.


2011 ◽  
Vol 295-297 ◽  
pp. 890-895
Author(s):  
Yan Dong ◽  
Yang Zhou ◽  
Xue Lin Han ◽  
Wei Jie Gu

Mg doped BaAl12O19:Mn2+ phosphor is one of the most efficient green phosphors for PDP. It is difficult to prepare the phosphor both have small particle size (< 3μm) and high luminescence. In the present work, a BaAl12O19:Mn2+ phosphor with small particle size was synthesized by the chemical co-precipitation method. Phase transformation and particle growth process during calcining process were investigated. The nucleation process was also discussed. The results show that, the phase transformation is complicated, the transition phases include BaCO3, γ-Al2O3, BaF2, BaAl2O4 and two phases contain Mn; The BaAl12O19 phase is formed from the reaction between BaAl2O4 phase and γ-Al2O3 phase, no a-Al2O3 phase appears during the entire process; The formation temperature of pure BaAl12O19 phase is 1200°C, which is lower than that in the high-temperature solid state reaction method. High efficiency BaAl12O19:Mn2+ phosphor with small particle size (< 2μm) and hexagonal flaky shape can be prepared by this method.


2010 ◽  
Vol 322 (21) ◽  
pp. 3470-3475 ◽  
Author(s):  
Yue Zhang ◽  
Zhi Yang ◽  
Di Yin ◽  
Yong Liu ◽  
ChunLong Fei ◽  
...  

2019 ◽  
Vol 546 (1) ◽  
pp. 48-56
Author(s):  
Ze Wu ◽  
Yang Song ◽  
Ruonan Zhang ◽  
Lianwei Shan ◽  
Limin Dong ◽  
...  

ChemInform ◽  
2011 ◽  
Vol 42 (13) ◽  
pp. no-no
Author(s):  
Yan Dong ◽  
Zhisen Wu ◽  
Xuelin Han ◽  
Rong Chen ◽  
Weijie Gu

Sign in / Sign up

Export Citation Format

Share Document