Ceramics PMN-PT-PFN for Multilayer Capacitors
We present the technology of the solid solution with formula (1-y)[(1-x)Pb(Mg1/3Nb2/3)O3-xPbTiO3]-yPb(Fe1/2Nb1/2)O3 where x=0.25, y=0.1 i.e. 0.9(0.75PMN-0.25PT)-0.1PFN. The addition of PFN decreases the temperature of final sintering and as a result such composition is interesting material for multilayer ceramic capacitors (MLCC). The powder of 0.9(0.75PMN-0.25PT)-0.1PFN has been obtained in three steps. In first step we obtained MgNb2O6. In second step FeNbO4 was obtained. In final third step the 0.9(0.75PMN-0.25PT)-0.1PFN was obtained from mixed powders MgNb2O6, FeNbO4 and PbO and TiO2. For obtained ceramics the following investigations have been made: XRD patterns, microstructure, EDS and main dielectric properties v.s. temperature. It has been stated that obtained ceramic powder is a good material for obtaining MLCC