Evaluation of Susceptibility to Stress Corrosion Cracking (SCC) in Sodium Chloride Solution of Weldments of Cold Rolled Type 316 Stainless Steel

Key Engineering Materials ◽

10.4028/www.scientific.net/kem.20-28.2249 ◽

1991 ◽

Vol 20-28 ◽

pp. 2249-2254

Author(s):

H.S. Khatak ◽

J.B. Gnanamoorthy ◽

K.A. Padmanabhan ◽

P. Rodriguez

Keyword(s):

Stainless Steel ◽

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

316 Stainless Steel ◽

Download Full-text

Stress Corrosion Cracking of SUS 304 Stainless Steel in Concentrated Sodium Chloride Solution at High Temperature

Corrosion engineering digest ◽

10.3323/jcorr1974.29.4_170 ◽

1980 ◽

Vol 29 (4) ◽

pp. 170-175

Author(s):

Makoto Kumada

Keyword(s):

Stainless Steel ◽

High Temperature ◽

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

304 Stainless Steel

Download Full-text

Stress Corrosion Cracking Behavior of Tungsten Heavy Alloys in Sodium Chloride Solution

CORROSION ◽

10.5006/1.3583959 ◽

1988 ◽

Vol 44 (7) ◽

pp. 435-442

Author(s):

J.-G. Chung ◽

D. J. Duquette

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

Cracking Behavior ◽

Heavy Alloys ◽

Tungsten Heavy Alloys

Download Full-text

The Influence of Chloride Content and Temperature on Crevice Corrosion and Stress Corrosion Cracking of Stainless Steels in Sodium Chloride Solution

Corrosion engineering digest ◽

10.3323/jcorr1974.28.11_577 ◽

1979 ◽

Vol 28 (11) ◽

pp. 577-583 ◽

Author(s):

Makoto Masuo ◽

Yutaka Ono ◽

Nobuo Ohashi

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Stainless Steels ◽

Crevice Corrosion ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Chloride Content ◽

Corrosion Cracking

Download Full-text

Test Method for Evaluating Stress-Corrosion Cracking of Stainless Alloys with Different Nickel Content in Boiling Acidified Sodium Chloride Solution

10.1520/g0123 ◽

2008 ◽

Author(s):

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Nickel Content ◽

Corrosion Cracking ◽

Download Full-text

Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

10.1520/g0103-97r05 ◽

2005 ◽

Author(s):

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

Cracking Resistance ◽

Download Full-text

Stress corrosion crack growth studies on AISI type 316 stainless steel in boiling acidified sodium chloride solution

Journal of Nuclear Materials ◽

10.1016/s0022-3115(96)00399-6 ◽

1996 ◽

Vol 238 (2-3) ◽

pp. 278-284 ◽

Author(s):

T.V. Vinoy ◽

H. Shaikh ◽

H.S. Khatak ◽

N. Sivaibharasi ◽

J.B. Gnanamoorthy

Keyword(s):

Stainless Steel ◽

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Crack ◽

Crack Growth ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

316 Stainless Steel ◽

Growth Studies ◽

Download Full-text

Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

10.1520/g0103-97r16 ◽

2016 ◽

Author(s):

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

Cracking Resistance ◽

Download Full-text

Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

10.1520/g0103-97r11 ◽

2011 ◽

Author(s):

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

Cracking Resistance ◽

Download Full-text

Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

10.1520/g0103-97 ◽

1997 ◽

Author(s):

Keyword(s):

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Chloride Solution ◽

Sodium Chloride Solution ◽

Corrosion Cracking ◽

Cracking Resistance ◽

Download Full-text

Effects of Thiosulfate on Susceptibility of Type 316 Stainless Steel to Stress Corrosion Cracking in 3.5% Aqueous Sodium Chloride

CORROSION ◽

10.5006/1.3290293 ◽

1997 ◽

Vol 53 (8) ◽

pp. 612-616 ◽

Author(s):

E. A. Ashour ◽

E. A. Abd El Meguid ◽

B. G. Ateya

Keyword(s):

Stainless Steel ◽

Sodium Chloride ◽

Stress Corrosion ◽

Stress Corrosion Cracking ◽

Corrosion Cracking ◽

Aqueous Sodium ◽

316 Stainless Steel

Download Full-text