The effect of restorative materials on the stress distribution of class V composite resin restorations - a 3D finite element investigation

The aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized class V cavities in all dentin margins. Teeth were divided into 5 equal groups according to the curing cycle. The cavities were incrementally restored with a composite resin (Single Bond/Z-100, 3M). Light curing was applied as follows: Group I: PAC light continuous-cycle curing at 1600 mW/cm² for 3s; Group II: PAC light step-cycle curing (2s at 800 mW/cm² then 4s at 1600 mW/cm²); Group III: QTH light continuous-cycle curing at 400 mW/cm² for 40s; Group IV: QTH light ramp-cycle curing (from 100 to 600 mW/cm² in 15s followed by 25s at 600 mW/cm²); Group V: QTH light pulse-delay curing (200 mW/cm² for 3s followed by 3 min delay then 600 mW/cm² for 30s). Teeth were stored in distilled water at 37ºC for 30 days and then subjected to thermocycling for 500 cycles at 5 and 55ºC. Root apices were sealed and teeth coated with nail varnish before they were immersed in 0.5% fuchsine red dye solution. Teeth were then sectioned and slices were scanned with a computer scanner to determine the area of dye leakage using a computer program (Image Tools). Images of tooth slices were also visually examined under magnification and dye penetration along the tooth/restoration interface was scored. Significant differences in the degree of dye penetration and leakage were detected between groups (p<.05). Groups I and II had significantly higher values of dye penetration and leakage than groups III, IV and V. In conclusion, the use of PAC light curing in a continuous or step cycle modes resulted in increased microleakage of Class V resin composite restorations compared with medium intensity QTH light curing. Pulse, ramp and continuous-cycle curing modes with QTH light resulted in similar degrees of microleakage.

Download Full-text

Sealing of adhesive systems in ferric sulfate-contaminated dentinal margins in class V composite resin restorations

Journal of Dental Research Dental Clinics Dental Prospects ◽

10.15171/joddd.2016.003 ◽

2016 ◽

Vol 10 (1) ◽

pp. 17-22 ◽

Cited By ~ 1

Author(s):

Niloofar Shadman ◽

Shahram Farzin Ebrahimi ◽

Najmeh Mollaie

Keyword(s):

Composite Resin ◽

Ferric Sulfate ◽

Adhesive Systems ◽

Class V ◽

Composite Resin Restorations ◽

Resin Restorations

Download Full-text

Comparison Of Microleakage Levels Of Class-V Hybrid Composite Resin Restorations

Balıkesır Health Sciences Journal ◽

10.5505/bsbd.2012.70288 ◽

2012 ◽

Vol 1 (3) ◽

pp. 110-116

Author(s):

Hakki Cenker Kucukesmen ◽

Cigdem Kucukesmen

Keyword(s):

Hybrid Composite ◽

Composite Resin ◽

Class V ◽

Composite Resin Restorations ◽

Resin Restorations

Download Full-text

Gambaran Penggunaan Resin Komposit dan Semen Ionomer Kaca Sebagai Bahan Restorasi di Poli Gigi Rumah Sakit Gunung Maria Tomohon Tahun 2012

e-GIGI ◽

10.35790/eg.1.2.2013.3215 ◽

2013 ◽

Vol 1 (2) ◽

Author(s):

Michael Sumolang

Keyword(s):

Composite Resin ◽

Resin Composite ◽

Glass Ionomer Cement ◽

Glass Ionomer ◽

Dental Resin ◽

Anterior Teeth ◽

Restorative Materials ◽

Composite Resin Restorations ◽

Ionomer Cement ◽

Resin Restorations

Gigi yang terserang kariesdapatdirawatdenganmenggunakanbahanrestorasi. Resin komposit dan semen ionomer kacamerupakanbahanyangdigunakanuntukperawatanrestorasi di poli gigi RS Gunung Maria Tomohon.Tujuanpenelitianiniuntukmengetahuigambaranpenggunaanbahanrestorasi resin kompositdan semen ionomerkaca di poligigi RSGunung Maria Tomohontahun 2012. Penelitianinimerupakanpenelitiandeskrpitif, data diambildarirekammedispasienrestorasidenganmetodetotal sampling.Data yang didapatyaitujumlah rekammedis pasien restorasi pada tahun 2012 sebanyak 268 danjumlahgigi yang direstorasisebanyak 387.Gigi yang direstorasimenggunakanbahan resin kompositsebanyak 207 gigi, sedangkangigi yang direstorasimenggunakan semen ionomerkacasebanyak 180 gigi.Hasilpenelitianinidibagiberdasarkanusia, jeniskelamin, elemengigidandiagnosa. Hasilpenelitianmenunjukankategoriusiadewasalebihseringmelakukanperawatanretorasi resin komposit dengan 145 gigi (70%) dan semen ionomerkaca dengan 106 gigi (58,8%) yang direstorasi, pasienperempuanlebihseringmelakukanperawatanrestorasiresin komposit dengan 117 (59,4%) dan semen ionomerkaca dengan 101 (56%) gigi yang direstorasi. Gigi bagian anterior seringdirestorasidengan menggunakan resin komposit dan gigibagian posterior seringdirestorasimenggunakan semen ionomerkaca.Hiperemiapulpamerupakanpenyakit yang paling didiagnosadan paling seringmendapatkanperawatanrestorasi resin komposit dengan 179 kasus (86%)dan semen ionomerkaca 157 kasus (87,3%).Kata Kunci:bahan restorasi, resin komposit, semen ionomerkacaABSTRACT Dental caries infected can be treated with restorative materials. Resin composites and glass ionomer cement is a material used for dental restorative treatment on poly Hospital Gunung Maria Tomohon. The purpose of this study to describe the use of composite resin restorations and glass ionomer cement in the teeth poly Hospital Gunung Maria Tomohon in 2012. This research is deskrpitif , data extracted from medical records of patients with restoration of total sampling.Data method obtained the restoration of the patient's medical record number in 2012 as many as 268 and the number of restored teeth as much as 387. Restored teeth using composite resin materials as much as 207 teeth, whereas the teeth restored with glass ionomer cement as many as 180 teeth. The results are divided based on age, sex, dental and diagnostic elements. The results showed the adult age category more often retorasi care dental resin composite with 145 (70 %) and glass ionomer cement with 106 teeth (58,8 %) were restored, female patients were more frequent maintenance of composite resin restorations with 117 (59,4 %) and glass ionomer cement with 101(56 %) restored teeth. Anterior teeth are restored using gigibagian posterior composite resin and glass ionomer cement seringdirestorasimenggunakan. Pulp hyperemia is the most diagnosed diseases and most often get care composite resin restorations with 179 cases (86 %) and glass ionomer cement 157 cases (87,3%). Keywords : restorative materials, composite resin, glass ionomer cement

Download Full-text

Effect of Cavity Disinfection with Chlorhexidine on Marginal Gap of Class V Composite Restorations Bonded with a Universal Adhesive Using Self-Etch and Etch-and-Rinse Bonding Strategy

Frontiers in Dentistry ◽

10.18502/fid.v17i1.3963 ◽

2020 ◽

Author(s):

Soodabeh Kimyai ◽

Narmin Mohammadi ◽

Mahmoud Bahari ◽

Elahe Pesyanian ◽

Farhood Pesyanian

Keyword(s):

Composite Resin ◽

Gap Size ◽

Marginal Gap ◽

Universal Adhesive ◽

Class V ◽

Etch And Rinse ◽

The Mean ◽

Composite Resin Restorations ◽

Self Etch ◽

Resin Restorations

Objectives: This in-vitro study aimed to evaluate the effect of cavity disinfection with chlorhexidine (CHX) on marginal gaps of Class V composite resin restorations bonded with a universal adhesive using self-etch and etch-and-rinse bonding strategy. Materials and Methods: Sixty sound human premolars were randomly assigned to two groups (n=30): group 1 (CHX) and group 2 (no CHX). Each group was divided into two subgroups (n=15) according to the bonding strategy of the universal adhesive (self-etch or etch-and-rinse). Class V cavities were prepared on the buccal surfaces of the teeth. The occlusal and gingival margins of the cavities were placed in enamel and dentin, respectively. In the first and second subgroups of both groups, the All-Bond Universal adhesive was applied with self-etch and etch-and-rinse bonding strategy, respectively. After restoration and thermocycling, the samples were sectioned, and marginal gaps at the gingival margins were measured in micrometer (µm) under a stereomicroscope. Two-way analysis of variance (ANOVA) was used to compare marginal gaps between the groups and the subgroups. Results: The mean marginal gap size was significantly affected by cavity disinfection (P=0.001) and bonding strategy (P=0.002). However, the interaction effect of these two factors on the mean marginal gap size was not significant (P=0.79). Conclusion: The use of CHX resulted in larger marginal gaps at the gingival margins of Class V composite resin restorations. Irrespective of disinfection, the self-etch bonding strategy resulted in larger marginal gaps compared to the etch-and-rinse bonding strategy.

Download Full-text