Linear friction welding (LFW) is an advanced joining technology used for manufacturing and repairing complex assemblies like blade integrated disks (blisks) of aeroengines. This paper presents an integrated multiphysics computational modelling for predicting the thermomechanical-microstructural processes of IN718 alloy (at the component-scale) during LFW. Johnson–Mehl–Avrami-Kolmogorov (JMAK) model was implemented for predicting the dynamic recrystallisation of γ grain, which was coupled with thermomechanical modelling of the LFW process. The computational modelling results of this paper agree well with experimental results from the literature in terms of γ grain size and weld temperature. Twenty different LFW process parameter configurations were systematically analysed in the computations by using the integrated model. It was found that friction pressure was the most influential process parameter, which significantly affected the dynamic recrystallisation of γ grains and weld temperature during LFW. The integrated multiphysics computational modelling was employed to find the appropriate process window of IN718 LFW.

Characterisation of Microstructure and Mechanical Properties of Linear Friction Welded α+β Titanium Alloy to Nitinol

A variable area nozzle integrated into the design of a high-bypass-ratio turbofan engine effectively saves up to 10% in aircraft fuel consumption. Additionally, noise emissions can be lowered at airports during take-off and landing by having better control of the nozzle diameter. Shape memory capabilities of Nitinol alloys could be availed in the form of actuators in the construction of such a nozzle. However, these Nitinol actuators must be joined to Ti-6Al-4V, a prominent alloy making up most of the rest of the nozzle. Because of the huge differences in the physical and metallurgical properties of these alloys, fusion welding is not as effective as solid-state welding. In the current study, a linear friction welding process was adopted to join Ti-6Al-4V to Nitinol successfully. The effect of friction welding on the evolution of weld macro and microstructures; hardness and tensile properties were studied and discussed. The macrostructure of Ti-6Al-4V and Nitinol’s dissimilar joint revealed flash formation mainly on the Ti-6Al-4V side due to its reduced flow strength at high temperatures. Optical microstructures revealed fine grains in Ti-6Al-4V immediately adjacent to the interface due to dynamic recrystallisation and strain hardening effects. In contrast, Nitinol remained mostly unaffected. An intermetallic compound (Ti2Ni) was seen to have formed at the interface due to the extreme rubbing action, and these adversely influenced the tensile strength and elongation values of the joints.