Growth of 6Li-enriched LiCl/BaCl2 eutectic as a novel neutron scintillator

In this study, Eu:6LiCl/BaCl2 with a high Li concentration was developed as a novel thermal neutron scintillator. Eu ions were doped as activators for the BaCl2 phase, and Eu:6LiCl/BaCl2 eutectics were grown via the vertical Bridgman–Stockbarger method in quartz ampoules (inner diameter = 4 mm). The Eu:6LiCl/BaCl2 eutectic exhibited a lamellar eutectic structure and optical transparency. The 400-nm emission due to the Eu2+ 4f–5d transition was observed in the BaCl2 phase by a cathode luminescence measurement. The light yield under neutrons was estimated to be over 20,200 photons/MeV. A pulse shape discrimination study was also performed using gamma and alpha-rays. The Eu:6LiCl/BaCl2 eutectic scintillator showed good potential of pulse shape discrimination.

Bridgman growth and electrical properties of Nd-doped PMN-PT single crystal with ultrahigh piezoelectricity

Using the polycrystalline material with a nominal composition of Nd0.01Pb0.985[(Mg1/3Nb2/3)0.70Ti0.30]O3, a Nd-doped PMN-PT single crystal has been grown successfully by vertical Bridgman process. The perovskite structure and the crystalline phase...

Growth and scintillation properties of LiBr/CeBr3 eutectic scintillator for neutron detection

The 6LiBr/CeBr3 eutectic scintillator for thermal neutron detection has been developed due to achieving high 6Li concentration. The eutectics were grown by vertical Bridgman method. Molar ratio of 6Li in 6LiBr/CeBr3 eutectic is 35 %, which is higher than that of commercial neutron scintillators such Ce:LiCaAlF6 and Ce:Cs2LiYCl6. The grown eutectic had lamellar-type eutectic structure extending along the growth direction and optical transparency. The grown eutectics showed an emission peak at 360 and 380 nm ascribed to Ce3+ 4f-5d transition from CeBr3 scintillation phase. The measurements of scintillation performance of the 6LiBr/CeBr3 were performed using x-ray, gamma-ray and neutron irradiation to evaluate its potential as a neutron scintillator.

Large size growth of terbium doped BaCl2/NaCl/KCl eutectic for radiation imaging

In this study, a large-size eutectic scintillator of Tb-doped BaCl2/NaCl/KCl was grown using the Czochralski (Cz) and halide vertical Bridgman methods (H-VB). The suitability of these two growth methods for growing the eutectic was compared. Finally, 1 diameter eutectic bulks were obtained using the H-VB method. The Tb3+-derived strongest intensity peak at approximately 550 nm was observed by X-ray irradiation. An approximately 3 × 3 mm transparent eutectic plate was cut and polished from the grown eutectic bulk. An α-ray imaging test was performed using the eutectic plate, a fiber optic plate, and an electron-multiplying CCD camera. The resolution performance for radiation-imaging applications was evaluated.