An Energy Based Model for the Influence of the Fibre-Matrix Interface Strength on the Interlaminar Fracture Toughness of UD-Composite Laminates

Author(s):  
J. Ivens ◽  
M. Wevers ◽  
I. Verpoest
2011 ◽  
Vol 194-196 ◽  
pp. 1697-1702
Author(s):  
Li Liang ◽  
Pu Rong Jia ◽  
Gui Qiong Jiao

Delamination is one of the important damage modes in the fiber-reinforced composite laminates. The interlaminar fracture toughness is the key parameter in delamination failure analysis of composites. The stress analysis by a finite element modeling has shown that the shear stress is very large near the ply splicing area. So the delamination failure is mainly dependent on the mode II fracture toughness. A new way of loading in tensile testing is proposed for the measurement of mode II fracture toughness. Specific specimen with splicing plies has been designed and used for the experiment. Testing study on the carbon-fiber-reinforced laminate with ply splicing was performed. Steady crack propagation has been seen by the tensile testing of the specimen. Mode II fracture toughness GIIC of the laminate has been determined by the experiment data analysis. The experiment and numerical analysis shows that the tensile testing for the measurement of mode II interlaminar fracture toughness is feasible.


2011 ◽  
Vol 121 (4) ◽  
pp. 2394-2405 ◽  
Author(s):  
Ryan J. Sager ◽  
Patrick J. Klein ◽  
Daniel C. Davis ◽  
Dimitris C. Lagoudas ◽  
Graham L. Warren ◽  
...  

Polymers ◽  
2021 ◽  
Vol 13 (9) ◽  
pp. 1437
Author(s):  
Alamry Ali ◽  
Andri Andriyana ◽  
Shukur Bin Abu Hassan ◽  
Bee Chin Ang

The development of advanced composite materials has taken center stage because of its advantages over traditional materials. Recently, carbon-based advanced additives have shown promising results in the development of advanced polymer composites. The inter- and intra-laminar fracture toughness in modes I and II, along with the thermal and electrical conductivities, were investigated. The HMWCNTs/epoxy composite was prepared using a multi-dispersion method, followed by uniform coating at the mid-layers of the CF/E prepregs interface using the spray coating technique. Analysis methods, such as double cantilever beam (DCB) and end notched flexure (ENF) tests, were carried out to study the mode I and II fracture toughness. The surface morphology of the composite was analyzed using field emission scanning electron microscopy (FESEM). The DCB test showed that the fracture toughness of the 0.2 wt.% and 0.4 wt.% HMWCNT composite laminates was improved by 39.15% and 115.05%, respectively, compared with the control sample. Furthermore, the ENF test showed that the mode II interlaminar fracture toughness for the composite laminate increased by 50.88% and 190%, respectively. The FESEM morphology results confirmed the HMWCNTs bridging at the fracture zones of the CF/E composite and the improved interlaminar fracture toughness. The thermogravimetric analysis (TGA) results demonstrated a strong intermolecular bonding between the epoxy and HMWCNTs, resulting in an improved thermal stability. Moreover, the differential scanning calorimetry (DSC) results confirmed that the addition of HMWCNT shifted the Tg to a higher temperature. An electrical conductivity study demonstrated that a higher CNT concentration in the composite laminate resulted in a higher conductivity improvement. This study confirmed that the demonstrated dispersion technique could create composite laminates with a strong interfacial bond interaction between the epoxy and HMWCNT, and thus improve their properties.