Obscure effect of cathodic polarization on rate of crack propagation during stress corrosion cracking of high-strength steels

1975 ◽  
Vol 10 (3) ◽  
pp. 233-235
Author(s):  
V. A. Marichev
Keyword(s):  
Crack Propagation ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
Cathodic Polarization ◽  
High Strength Steels ◽  
High Strength ◽  
Corrosion Cracking

Stress Corrosion Cracking of High Strength Steels

1995 ◽  
Author(s):  
Eun U. Lee ◽  
Henry Sanders ◽  
Bhaskar Sarkar
Keyword(s):  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
High Strength Steels ◽  
High Strength ◽  
Corrosion Cracking

Stress Corrosion Cracking of High Strength Steels and Titanium Al in Chloride Solutions at Ambient Temperature

CORROSION ◽  
1967 ◽  
Vol 23 (5) ◽  
pp. 142-148 ◽  
Author(s):  
M. H. PETERSON ◽  
B. F. BROWN ◽  
R. L. NEWBEGIN ◽  
R. E. GROOVER
Keyword(s):  
Ambient Temperature ◽  
Stress Corrosion ◽  
Stress Corrosion Cracking ◽  
High Strength Steels ◽  
High Strength ◽  
Corrosion Cracking ◽  
Chloride Solutions