The SOFC interconnect materials La[Formula: see text]Sr[Formula: see text]Cr[Formula: see text]O[Formula: see text] [Formula: see text]–[Formula: see text] were prepared using an auto-ignition process. The influences of Cr deficiency on their sintering, thermal expansion and electrical properties were investigated. All the samples were pure perovskite phase after sintering at 1400[Formula: see text]C for 4 h. The cell volume of La[Formula: see text]Sr[Formula: see text]Cr[Formula: see text]O[Formula: see text] decreased with increasing Cr deficient content. The relative density of the sintered bulk samples increased from 93.2% [Formula: see text] to a maximum value of 94.7% [Formula: see text] and then decreased to 87.7% [Formula: see text]. The thermal expansion coefficients of the sintered bulk samples were in the range of [Formula: see text]–[Formula: see text] (30–1000[Formula: see text]C), which are compatible with that of YSZ. Among the investigated samples, the sample with 0.02 Cr deficiency had a maximum conductivity of 40.4 Scm[Formula: see text] and the lowest Seebeck coefficient of 154.8 [Formula: see text]VK[Formula: see text] at 850[Formula: see text]C in pure He. The experimental results indicate that La[Formula: see text]Sr[Formula: see text]Cr[Formula: see text]O[Formula: see text] has the best properties and is much suitable for SOFC interconnect material application.
Analysis of rapid compression machine facility effects on the auto-ignition of ethanol