Synergistic Effects of Temperature, Oxidation and Stress Level on Fatigue Damage Evolution and Lifetime Prediction of Cross-Ply SiC/CAS Ceramic-Matrix Composites Through Hysteresis-Based Parameters

Journal of Materials Engineering and Performance ◽

10.1007/s11665-017-3028-5 ◽

2017 ◽

Vol 26 (12) ◽

pp. 5681-5693 ◽

Author(s):

Longbiao Li

Keyword(s):

Fatigue Damage ◽

Stress Level ◽

Damage Evolution ◽

Synergistic Effects ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Lifetime Prediction ◽

Matrix Composites ◽

Temperature Oxidation ◽

Effects Of Temperature

Download Full-text

Synergistic Effects of Temperature, Oxidation and Multicracking Modes on Damage Evolution and Life Prediction of 2D Woven Ceramic-Matrix Composites under Tension-Tension Fatigue Loading

Applied Composite Materials ◽

10.1007/s10443-016-9567-3 ◽

2016 ◽

Vol 24 (4) ◽

pp. 965-981 ◽

Author(s):

Li Longbiao

Keyword(s):

Damage Evolution ◽

Life Prediction ◽

Synergistic Effects ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Fatigue Loading ◽

Matrix Composites ◽

Temperature Oxidation ◽

Effects Of Temperature

Download Full-text

Synergistic effects of temperature, oxidation, and stress level on fatigue hysteresis behavior of cross-ply ceramic-matrix composites at room and elevated temperatures under cyclic loading

Journal of the Australian Ceramic Society ◽

10.1007/s41779-017-0121-z ◽

2017 ◽

Vol 54 (1) ◽

pp. 11-22 ◽

Author(s):

Li Longbiao

Keyword(s):

Cyclic Loading ◽

Stress Level ◽

Elevated Temperatures ◽

Synergistic Effects ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Matrix Composites ◽

Temperature Oxidation ◽

Hysteresis Behavior ◽

Effects Of Temperature

Download Full-text

Thermal cyclic fatigue damage evolution of fiber-reinforced ceramic-matrix composites under constant loading

Composite Interfaces ◽

10.1080/09276440.2021.1960678 ◽

2021 ◽

pp. 1-20

Author(s):

Longbiao Li ◽

Pascal Reynaud ◽

Gilbert Fantozzi

Keyword(s):

Fatigue Damage ◽

Damage Evolution ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Cyclic Fatigue ◽

Matrix Composites ◽

Fiber Reinforced ◽

Constant Loading

Download Full-text

In-phase thermomechanical fatigue damage evolution of long fiber-reinforced ceramic-matrix composites using fatigue hysteresis-based damage parameters

International Journal of Mechanical Sciences ◽

10.1016/j.ijmecsci.2018.03.005 ◽

2018 ◽

Vol 140 ◽

pp. 189-199 ◽

Author(s):

Li Longbiao

Keyword(s):

Fatigue Damage ◽

Damage Evolution ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Thermomechanical Fatigue ◽

Matrix Composites ◽

Fiber Reinforced

Download Full-text

Synergistic Effects of Temperature and Oxidation on Matrix Cracking in Fiber-Reinforced Ceramic-Matrix Composites

Applied Composite Materials ◽

10.1007/s10443-016-9535-y ◽

2016 ◽

Vol 24 (3) ◽

pp. 691-715 ◽

Author(s):

Li Longbiao

Keyword(s):

Synergistic Effects ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Matrix Cracking ◽

Matrix Composites ◽

Fiber Reinforced ◽

Effects Of Temperature

Download Full-text

Synergistic effects of stochastic loading stress and time on stress-rupture damage evolution and lifetime of fiber-reinforced ceramic-matrix composites at intermediate temperatures

Ceramics International ◽

10.1016/j.ceramint.2019.11.283 ◽

2020 ◽

Vol 46 (6) ◽

pp. 7792-7812 ◽

Author(s):

Li Longbiao

Keyword(s):

Damage Evolution ◽

Synergistic Effects ◽

Stress Rupture ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Matrix Composites ◽

Fiber Reinforced ◽

Stochastic Loading

Download Full-text

Synergistic effects of temperature, oxidation, loading frequency and stress-rupture on damage evolution of cross-ply ceramic-matrix composites under cyclic fatigue loading at elevated temperatures in oxidizing atmosphere

Engineering Fracture Mechanics ◽

10.1016/j.engfracmech.2017.03.013 ◽

2017 ◽

Vol 175 ◽

pp. 15-30 ◽

Author(s):

Longbiao Li

Keyword(s):

Elevated Temperatures ◽

Synergistic Effects ◽

Stress Rupture ◽

Ceramic Matrix Composites ◽

Fatigue Loading ◽

Cyclic Fatigue ◽

Loading Frequency ◽

Matrix Composites ◽

Temperature Oxidation ◽

Effects Of Temperature

Download Full-text

Synergistic Effects of Frequency and Temperature on Damage Evolution and Life Prediction of Cross-Ply Ceramic Matrix Composites under Tension-Tension Fatigue Loading

Applied Composite Materials ◽

10.1007/s10443-016-9578-0 ◽

2016 ◽

Vol 24 (5) ◽

pp. 1061-1088 ◽

Author(s):

Li Longbiao

Keyword(s):

Damage Evolution ◽

Life Prediction ◽

Synergistic Effects ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Fatigue Loading ◽

Matrix Composites

Download Full-text

Temperature-Dependent Fatigue Damage Evolution of Fiber-Reinforced Ceramic-Matrix Composites

10.1115/1.0002476v ◽

2021 ◽

Author(s):

Longbiao Li

Keyword(s):

Fatigue Damage ◽

Damage Evolution ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Matrix Composites ◽

Fiber Reinforced ◽

Temperature Dependent

Download Full-text

Fatigue damage and lifetime prediction of fiber-reinforced ceramic-matrix composites

Fatigue Life Prediction of Composites and Composite Structures ◽

10.1016/b978-0-08-102575-8.00008-5 ◽

2020 ◽

pp. 269-333

Author(s):

Longbiao Li

Keyword(s):

Fatigue Damage ◽

Ceramic Matrix Composites ◽

Ceramic Matrix ◽

Lifetime Prediction ◽

Matrix Composites ◽

Fiber Reinforced

Download Full-text