60CaO-30P2O5-(10 ̶ x)Nb2O5-xTiO2 (x = 0 ~ 10, mol%) glasses were prepared in order to obtain biomaterials with high chemical durability and therapeutic ions releasability. Dissolution test of these glasses using Tris buffer solution showed the controlled release of niobate ions from Nb2O5-containing glasses and the formation of calcium titanate in some of them. These behavior might induce positive effects for bone regeneration.
Boroaluminosilicate glasses containing La2O3 were prepared by the normal quenching method. The glass transition temperatures (Tg) were measured by differential scanning calorimetry (DSC). The structural role of RO was investigated by nuclear magnetic resonance (NMR). Chemical durability was evaluated by weight losses of glass samples after immersion in HC1 solution. High resolution scanning electron microscopy (HR-SEM) was used to examine the surface micrographs of corroded glass samples. The dielectric constant and tangent loss were measured in the frequency range 10–106 Hz. The results revealed that chemical durability and dielectric properties increased with increasing La2O3 content.