In this study, a new Fe-6Mn-4Al-0.4C high strength medium manganese hot rolled steel sheet was designed. The influence mechanism of the intercritical annealing (IA) temperature on microstructure evolution and mechanical properties of experimental steel were studied by SEM and XRD. The experimental steel was held for 30 minutes at 640°C, 680°C, 720°C, 760°C, 800°C, respectively. When the annealing temperature was 640°C, cementite particles precipitated between the austenite and ferrite phase boundary. As the annealing temperature increased, the cementite gradually dissolved and disappeared, the fraction of lamellar austenite increased significantly. When the annealing temperature is 800°C, the coarse equiaxed austenite and ferrite appeared. The yield strength (YS) decreased, the product of strength and elongation (PSE) and total elongation (TE) both increased first and then decreased, while the ultimate tensile strength (UTS) showed the opposite trend. The experimental steel exhibited excellent comprehensive mechanical properties after held at 760°C for 30 min. The UTS was 870 MPa, the YS was 703 MPa, and the TE was 77 %, the PSE was 67 GPa·%.
Mechanical Properties and Precipitation Behavior of High Strength Hot-Rolled Ferritic Steel Containing Nb and V