Strategy for the Improvement of the Mechanical Properties of Cellulose Nanofiber-Reinforced High-Density Polyethylene Nanocomposites Using Diblock Copolymer Dispersants

2017 ◽  
Vol 9 (50) ◽  
pp. 44079-44087 ◽  
Author(s):  
Keita Sakakibara ◽  
Yoshihito Moriki ◽  
Hiroyuki Yano ◽  
Yoshinobu Tsujii
Keyword(s):  
Mechanical Properties ◽  
Diblock Copolymer ◽  
High Density Polyethylene ◽  
High Density ◽  
Cellulose Nanofiber

Pre-Fibrillation of Pulps to Manufacture Cellulose Nanofiber Reinforced High-Density Polyethylene using the Dry-Pulp Direct Kneading Method

2021 ◽  
Author(s):  
Yuko Igarashi ◽  
Akihiro Sato ◽  
Hiroaki Okumura ◽  
Fumiaki Nakatsubo ◽  
Takashi Kuboki ◽  
...  
Keyword(s):  
High Density Polyethylene ◽  
Coefficient Of Thermal Expansion ◽  
Tensile Modulus ◽  
Cellulose Fibers ◽  
High Density ◽  
Cellulose Nanofiber ◽  
Feed Material ◽  
Alkenyl Succinic Anhydride ◽  
Melt Compounding ◽  
Kneading Method

Abstract The dry-pulp direct-kneading method is an industrially viable, low-energy process to manufacture cellulose nanofiber (CNF) reinforced polymer composites, where chemically modified pulps can be nanofibrillated and dispersed uniformly in the polymer matrix during melt-compounding. In this study, cellulose fibers with different sizes, ranging from surface-fibrillated pulps with 20 µm in width to fine CNFs with 20 nm in width were prepared from softwood bleached kraft pulps (NBKPs) using a refiner and high-pressure homogenizer (HPH). These cellulose fibers were modified with alkenyl succinic anhydride (ASA), and then dried. The dried ASA-treated cellulose fibers were used as a feed material for melt-compounding in the dry-pulp direct kneading method to fabricate CNF reinforced high-density polyethylene (HDPE). When surface-fibrillated pulps were employed as a feed material, the pulps were nanofibrillated and dispersed uniformly in the HDPE matrix during the melt-compounding, and the composites had much better properties (i.e., much higher tensile modulus and strength and much lower coefficient of thermal expansion) than the composites produced using the pulps without pre-fibrillation. However, when CNFs were used as a feed material, the CNFs were shortened and agglomerated during the melt-compounding, thus deteriorating the properties of the composites. The study concludes that the pre-fibrillation of pulps had a significant impact on the morphology and properties of the composites. Unexpectedly, the surface-fibrillated pulp, which can be produced cost-effectively using a refiner at an industry scale, was a more suitable form than the CNF as a feed material for melt-compounding in the dry-pulp direct kneading method.

Effect of flow forming on mechanical properties of high density polyethylene pipes

2015 ◽  
Vol 19 ◽  
pp. 155-162 ◽  
Author(s):  
Amin Abedini ◽  
Payam Rahimlou ◽  
Taghi Asiabi ◽  
Samrand Rash Ahmadi ◽  
Taher Azdast
Keyword(s):  
Mechanical Properties ◽  
High Density Polyethylene ◽  
High Density ◽  
Flow Forming ◽  
Polyethylene Pipes
Sign in / Sign up

Export Citation Format

Share Document