1-Methoxy-2-propanol was found to be a promising safe alternative to carcinogenic and teratogenic 2-methoxyethanol as solvent for chemical solution deposition of {100}-oriented lead zirconate titanate thin films on platinized silicon.
In this study, a finely patterned lead zirconate titanate (PZT) film is fabricated by a combination of inkjet printing (IJP), chemical solution deposition (CSD), and surface energy controlling technology. The PZT film, which can be used as an actuator, has enough thickness after iterating the set of surface treatment, inkjet deposition, and baking. We confirmed the electrical characteristic of this film and drop ejection from inkjet head using it.
ABSTRACTInfluences of the B-site substitution using Dy3+ ion on the crystal structure and ferroelectric properties of lead zirconate titanate (PZT) films were investigated. Dy3+-substituted PZT films with nominal chemical compositions of Pb1.00Dyx (Zr0.40Ti0.60)1-(3x/4)O3 (x = 0 ∼ 0.06) were fabricated by a chemical solution deposition (CSD). Polycrystalline PZT films with preferential orientation of (111)PZT were obtained on (111)Pt/TiO2/SiO2/(100)Si substrates, while epitaxially-grown (111)PZT films were fabricated on (111)SrRuO3//(111)Pt//(100)YSZ//(100)Si substrate. Ratio of PZT lattice parameters (c/a), which corresponds to its crystal anisotropy, was enhanced by the Dy3+-substitution with x = 0.02. Spontaneous polarization (Ps) of Dy3+-substituted PZT film (x = 0.02) along polar [001] axis of PZT lattice was estimated from saturation polarization (Psat) value of the epitaxially-grown (111)PZT film on (111)SrRuO3//(111)Pt//(100)YSZ//(100)Si to be 84 μC/cm2 that was significantly larger than that of non-substituted PZT (= 71 μC/cm2). We concluded that the enhancement of Ps value could be achieved by the Dy3+-substitution that promoted the crystal anisotropy of PZT lattice.
Growth of {100}-oriented lead zirconate titanate thin films mediated by a safe solvent