Biphasic calcium phosphate loading on polycaprolactone/poly(lacto-co-glycolic acid) membranes for improved tensile strength, in vitro biocompatibility, and in vivo tissue regeneration

This study demonstrates the utility of camphene as the pore-regulating agent for phase separation-based 3D plotting to produce hierarchical macro/micro-porous poly(ε-caprolactone) (PCL)–calcium phosphate (CaP) composite scaffolds, specifically featuring highly microporous surfaces. Unlike conventional particulate porogens, camphene is highly soluble in acetone, the solvent for PCL polymer, but insoluble in coagulation medium (water). In this study, this unique characteristic supported the creation of numerous micropores both within and at the surfaces of PCL and PCL–CaP composite filaments when using high camphene contents (40 and 50 wt%). In addition, the incorporation of the CaP particles into PCL solutions did not deteriorate the formation of microporous structures, and thus hierarchical macro/micro-porous PCL–CaP composite scaffolds could be successfully produced. As the CaP content increased, the in vitro biocompatibility, apatite-forming ability, and mechanical properties (tensile strength, tensile modulus, and compressive modulus) of the PCL–CaP composite scaffolds were substantially improved.

Download Full-text

Biocompatibility of Surface-Modified Biphasic Calcium Phosphate/Poly-L-Lactide Biocomposite in vitro and in vivo

Journal of Material Science and Technology ◽

10.1016/s1005-0302(10)60119-3 ◽

2010 ◽

Vol 26 (8) ◽

pp. 754-758 ◽

Cited By ~ 8

Author(s):

Weizhong Yang ◽

Guangfu Yin ◽

Dali Zhou ◽

Jianwen Gu ◽

Yadong Li ◽

...

Keyword(s):

Calcium Phosphate ◽

Biphasic Calcium Phosphate ◽

Surface Modified

Download Full-text

Development of injectable chitosan/biphasic calcium phosphate bone cement and in vitro and in vivo evaluation

Biomedical Materials ◽

10.1088/1748-605x/ab8441 ◽

2020 ◽

Vol 15 (5) ◽

pp. 055038

Author(s):

Sirirat T. Rattanachan ◽

Nuan La-ong Srakaew ◽

Paritat Thaitalay ◽

Oranich Thongsri ◽

Rawee Dangviriyakul ◽

...

Keyword(s):

Calcium Phosphate ◽

Bone Cement ◽

Biphasic Calcium Phosphate ◽

In Vivo Evaluation ◽

Calcium Phosphate Bone Cement

Download Full-text

A novel hybrid multichannel biphasic calcium phosphate granule-based composite scaffold for cartilage tissue regeneration

Journal of Biomaterials Applications ◽

10.1177/0885328217741757 ◽

2017 ◽

Vol 32 (6) ◽

pp. 775-787 ◽

Cited By ~ 5

Author(s):

Albert Jung ◽

Preeti Makkar ◽

Jhaleh Amirian ◽

Byong-Taek Lee

Keyword(s):

Compressive Strength ◽

Calcium Phosphate ◽

Biphasic Calcium Phosphate ◽

Composite System ◽

Composite Scaffold ◽

Cartilage Regeneration ◽

Cartilage Tissue ◽

In Vitro Biocompatibility ◽

Surface Modified

The objective of the present study was to develop a novel hybrid multichannel biphasic calcium phosphate granule (MCG)-based composite system for cartilage regeneration. First, hyaluronic acid-gelatin (HG) hydrogel was coated onto MCG matrix (MCG-HG). Poly(lactic-co-glycolic acid) (PLGA) microspheres was separately prepared and modified with polydopamine subsequent to BMP-7 loading (B). The surface-modified microspheres were finally embedded into MCG-HG scaffold to develop the novel hybrid (MCG-HG-PLGA-PD-B) composite system. The newly developed MCG-HG-PLGA-PD-B composite was then subjected to scanning electron microscopy, energy dispersive X-ray spectroscopy, Fourier Transform infrared spectroscopy, porosity, compressive strength, swelling, BMP-7 release and in-vitro biocompatibility studies. Results showed that 60% of BMP-7 retained on the granular surface after 28 days. A hybrid MCG-HG-PLGA-PD-B composite scaffold exhibited higher swelling and compressive strength compared to MCG-HG or MCG. In-vitro studies showed that MCG-HG-PLGA-PD-B had improved cell viability and cell proliferation for both MC3T3-E1 pre-osteoblasts and ATDC5 pre-chondrocytes cell line with respect to MCG-HG or MCG scaffold. Our results suggest that a hybrid MCG-HG-PLGA-PD-B composite scaffold can be a promising candidate for cartilage regeneration applications.

Download Full-text