Effect of Welding Heat Input on Microstructure and Properties of Coarse Grain Zone in Heat Affected Zone of Ultra-Low Carbon Bainitic Steel

AbstractThe microstructure evolution and impact toughness of the coarse grain heat-affected zone (CGHAZ) of TiNbV microalloyed steels were investigated by using a thermal simulation test. The samples were treated with various simulated welding thermal cycles. The phase constituents and grain sizes were analyzed by using electron backscatter diffraction analysis. The microstructure of the CGHAZ of the treated samples consisted of ferrite, acicular ferrite, pearlite, and bainite. The samples have a higher impact toughness under a lower welding heat input. This is because the microstructure of the CGHAZ is dominated by the higher volume fraction of the high-angle grain boundaries of acicular ferrites. The presence of bainite and coarsening grains are two key factors deteriorating the toughness of the CGHAZ of TiNbV microalloyed steels. The volume fraction of bainite sharply increased as the welding heat input increased, leading to a decrease in the impact toughness of the CGHAZ. For a higher welding heat input, both the severe coarsening of the grain size and a higher bainite content would result in poor impact toughness.

Download Full-text

Continuous Cooling Transformation Diagram, Microstructures, and Properties of the Simulated Coarse-Grain Heat-Affected Zone in a Low-Carbon Bainite E550 Steel

Metals ◽

10.3390/met9090939 ◽

2019 ◽

Vol 9 (9) ◽

pp. 939 ◽

Cited By ~ 1

Author(s):

Yun Zong ◽

Chun-Ming Liu

Keyword(s):

Impact Toughness ◽

Cooling Rate ◽

Vickers Hardness ◽

Heat Affected Zone ◽

Granular Bainite ◽

Coarse Grain ◽

Low Carbon ◽

Transformation Diagram ◽

Lath Bainite ◽

Continuous Cooling Transformation Diagram

In order to provide important guidance for controlling and obtaining the optimal microstructures and mechanical properties of a welded joint, the continuous cooling transformation diagram of a new low-carbon Nb-microalloyed bainite E550 steel in a simulated coarse-grain heat-affected zone (CGHAZ) has been constructed by thermal dilatation method in this paper. The welding thermal simulation experiments were conducted on a Gleeble-3800 thermo-mechanical simulator. The corresponding microstructure was observed by a LEICA DM2700M. The Vickers hardness (HV) and the impact toughness at −40 °C were measured according to the ASTM E384 standard and the ASTM E2298 standard, respectively. The experimental results may indicate that the intermediate temperature phase transformation of the whole bainite can occur in a wide range of cooling rates of 2–20 °C/s. In the scope of cooling rates 2–20 °C/s, the microstructure of the heat-affected zone (HAZ) mainly consists of lath bainite and granular bainite. Moreover, the proportion of lath bainite increased and granular bainite decreased as the cooling rate increasing. There is a spot of lath martensite in the microstructure of HAZ when the cooling rate is above 20 °C/s. The Vickers hardness increases gradually with the increasing of the cooling rate, and the maximum hardness is 323 HV10. When the cooling time from 800 °C to 500 °C (t8/5) is 5–15 s, it presents excellent −40 °C impact toughness (273–286 J) of the CGHAZ beyond the base material (163 J).