ABSTRACT
The aim of this in vitro study was to compare the cyclic fatigue resistance of three single-use nickel-titanium (NiTi) instruments (One Shape, Reciproc and Wave One) after immersion in sodium hypochlorite (NaOCl) solution over several time periods. A total of 135 One Shape, Reciproc R25 and Wave One Primary were tested. The 45 files of the same brand were randomly assigned to three groups (n = 15) and submitted to the following immersion protocol: 1 minute in 5% NaOCl at 37°C, 5 minutes in 5% NaOCl at 37°C, no immersion (as control). Cyclic fatigue test was performed rotating/reciprocating all instruments in a stainless steel curved artificial canal (60° angle of curvature and 5 mm radius). The number of cycles to fracture (NCF) was determined by measuring the time to fracture. The data were compared for differences by using 2-way analysis of variance (p < 0.05). In general, resistance to cyclic fatigue was not significantly affected by immersion in NaOCl. Reciproc R2 showed the highest cyclic fatigue resistance in all groups compared to One Shape and Wave One. Immersion in NaOCl for 1 or 5 minutes did not reduce the cyclic fatigue resistance of NiTi single-use instruments significantly. Reciproc were more resistant, but the new rotary single-use One Shape instruments showed mechanical resistance similar to NiTi files developed for reciprocating motion.
How to cite this article
Dagna A, Beltrami R, Colombo M, Chiesa M, Bianchi S, Poggio C. Cyclic Fatigue Resistance of Three Single-use NiTi Instruments after Immersion in Sodium Hypochlorite. Int J Experiment Dent Sci 2014;3(2):67-72.
An in-vitro comparative study of cyclic fatigue resistance of twisted files, Hyflex cm, Hyflex edm and Edgefile X3 after immersion in sodium hypochlorite and/or sterilization