Influence of impurity and alloying elements on high temperature oxidation resistance of E110 type zirconium alloys

2021 ◽  
pp. 27-32
Author(s):  
A. B. Rozhnov ◽  
◽  
S. A. Nikulin ◽  
V. A. Belov ◽  
E. V. Li ◽  
...  
Keyword(s):  
High Temperature ◽  
High Temperature Oxidation ◽  
Structural Phase ◽  
Zirconium Alloys ◽  
Type Alloy ◽  
Temperature Oxidation ◽  
Structural Phase State ◽  
Local Oxidation ◽  
Oxidation Depth ◽  
Content Of Oxygen

The structural-phase state has been investigated and content of oxygen and hydrogen in the E110 type alloy after high-temperature oxidation simulating an accident of the LOCA type has been determined. Tubular samples with a diameter of 9.13 mm and a wall thickness of 0.7 mm from the Zr—1% Nb alloy obtained on the electrolytic zirconium basis (E110), the zirconium sponge basis (E110G), and from a modified alloy Zr—1% Nb—0.12% Fe—0.13% O (E110M) were selected for the study. The samples were subjected to a steam oxidation at a temperature of 1100 °C to 18% local oxidation depth. It was found that the E110G alloy based on a zirconium sponge absorbed oxygen and hydrogen less under LOCA conditions.

Vacuum-arc chromium-based coatings for protection of zirconium alloys from the high-temperature oxidation in air

2015 ◽  
Vol 465 ◽  
pp. 400-406 ◽  
Author(s):  
А.S. Kuprin ◽  
V.А. Belous ◽  
V.N. Voyevodin ◽  
V.V. Bryk ◽  
R.L. Vasilenko ◽  
...  
Keyword(s):  
High Temperature ◽  
High Temperature Oxidation ◽  
Zirconium Alloys ◽  
Vacuum Arc ◽  
Temperature Oxidation ◽  
Oxidation In Air

scholarly journals HIGH-TEMPERATURE OXIDATION OF CHROME-NICKEL ALLOY

2020 ◽  
Vol 28 ◽  
pp. 8-14
Author(s):  
Adéla Chalupová ◽  
Martin Steinbrück ◽  
Mirco Grosse ◽  
Jakub Krejčí ◽  
Martin Ševeček
Keyword(s):  
High Temperature ◽  
Melting Point ◽  
High Temperature Oxidation ◽  
Zirconium Alloys ◽  
Temperature Oxidation ◽  
Ni Alloy ◽  
Institute Of Technology ◽  
Kinetics Of ◽  
Karlsruhe Institute ◽  
Nuclear Applications

The investigations in this paper deal with the Cr-Ni alloy. The material has been recently proposed as a potential ATF concept, primarily due to its behaviour under high-temperature oxidation. A set of experiments to determine the melting point and describe the oxidation kinetics of the Cr-Ni alloy were performed in Karlsruhe Institute of Technology. Presented results reveal its superb oxidation resistance comparing to zirconium alloys. Therefore, the alloy has a great potential for nuclear applications.

Effect of Copper Addition on the High Temperature Oxidation of Zirconium Alloy ZrNbMoGe for Advanced Reactor Fuel Cladding Material

2014 ◽  
Vol 896 ◽  
pp. 617-620 ◽  
Author(s):  
Bernardus Bandriyana ◽  
Djoko Hadi Prajitno ◽  
Arbi Dimyati
Keyword(s):  
High Temperature ◽  
Zirconium Alloy ◽  
High Temperature Oxidation ◽  
Zirconium Alloys ◽  
Magnetic Suspension ◽  
Pressurized Water ◽  
Temperature Oxidation ◽  
Copper Addition ◽  
Effect Of Copper ◽  
Cladding Material

The zirconium alloys ZrNbMoGe have been developed with the aim to improve its high temperature oxidation for employment as a cladding material in Pressurized Water Reactor (PWR) and to extend the over all fuel burn-up. In this paper the effect of Cu addition on the high temperature oxidation behavior of ZrNbMoGe alloy was investigated. The zirconium alloy was produced by melting the zirconium-niobium-molybdenum-germanium and copper-sponge in an arc furnace in an argon environment by the temperature higher than 1850C. The weight percentages of the elements were 2.50 wt.% Nb, 0.5 wt.% Mo, 0.1 wt.% Ge, 0.5 wt.% Cu and Zr in balanced. The oxidation test was carried out in the Magnetic Suspension Balance (MSB) workstation. Two specimens of ZrNbMoGe alloys without and with Cu addition were oxidized in atmosphere at temperature of 500 °C and 700 °C for 8 hours. The results show the oxidation kinetics followed the parabolic rate law. The difference of oxidation behaviors of the two specimens were considered to be caused by the formation of different kind of oxide layers due to the Cu addition.

Simulation of the β→α(O) Phase Transformation due to Oxygen Diffusion during High Temperature Oxidation of Zirconium Alloys

2011 ◽  
Vol 172-174 ◽  
pp. 652-657 ◽  
Author(s):  
Caroline Toffolon-Masclet ◽  
Clara Desgranges ◽  
Carolina Corvalan-Moya ◽  
Jean Christophe Brachet
Keyword(s):  
Phase Transformation ◽  
High Temperature ◽  
Oxide Layer ◽  
Oxygen Diffusion ◽  
High Temperature Oxidation ◽  
Equilibrium Concentration ◽  
Zirconium Alloys ◽  
Numerical Code ◽  
Temperature Oxidation ◽  
O Phase

The EKINOX numerical code, formerly developed to simulate high temperature oxidation of Ni alloys, has been recently adapted to solve out the issue of high temperature oxidation of Zirconium alloys. This numerical code is a one dimensional model that simulates the growth of an oxide layer using a specific algorithm for moving boundaries problem. In order to simulate the oxygen diffusion inside Zr alloys, an adaptation of the EKINOX code was necessary. It consisted in adding, first, a non-null oxygen equilibrium concentration in the substrate and second, a new interface in order to simulate the β/α(O) phase transformation due to oxygen diffusion. In this study, EKINOX has also been coupled with the thermodynamic database for zirconium alloys ZIRCOBASE (thermocalc formalism) in order to obtain accurate concentrations values in each phases (considering local equilibrium at each interface). The present paper illustrates the simulation ability of the code by comparing experimental and calculated oxygen diffusion profiles corresponding to different cases, from isothermal oxidations at high temperature (900 < T < 1250°C) to the study of dissolution kinetics of a pre-transient oxide layer under a neutral environment. The influence of pre-hydriding from a few hundreds up to thousands weight-ppm is also derived from the calculations.

Sign in / Sign up

Export Citation Format

Share Document