ISO 185/JL/350

Alloy Digest ◽  
2021 ◽  
Vol 70 (9) ◽  
Keyword(s):  
Thermal Conductivity ◽  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
High Strength ◽  
Heat Treating ◽  
Gray Cast ◽  
Spheroidal Graphite ◽  
Cast Irons ◽  
Test Pieces

Abstract ISO 185/JL/350 is a higher-tensile-strength gray cast iron that has a pearlitic matrix, and a tensile strength of 350–450 MPa (51–65 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. It provides a combination of high strength while still maintaining good thermal conductivity compared with other types of cast iron. This grade approaches the maximum tensile strength attainable in gray cast iron. Applications therefore tend to be confined to those where thermal conductivity requirements in service preclude the use of one of the other higher-strength materials such as spheroidal graphite cast irons, which have inferior thermal properties. This datasheet provides information on composition, physical properties, and tensile properties. It also includes information on wear resistance as well as casting and heat treating. Filing Code: CI-85. Producer or source: International Organization for Standardization.

ISO 185/JL/300

Alloy Digest ◽  
2021 ◽  
Vol 70 (6) ◽  
Keyword(s):  
Thermal Conductivity ◽  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
High Strength ◽  
Heat Treating ◽  
Gray Cast ◽  
Spheroidal Graphite ◽  
Cast Irons ◽  
Test Pieces

Abstract ISO 185/JL/300 is a higher-tensile-strength gray cast iron that has a pearlitic matrix; it has a tensile strength of 300–400 MPa (44–58 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. It provides high strength while still maintaining good thermal conductivity compared with other types of cast iron. This grade approaches the maximum tensile strength attainable in gray cast iron. Applications therefore tend to be confined to those where thermal conductivity requirements in service preclude the use of one of the other higher-strength materials such as spheroidal graphite cast irons, which have inferior thermal properties. This datasheet provides information on composition, physical properties, and tensile properties. It also includes information on casting and heat treating. Filing Code: CI-82. Producer or source: International Organization for Standardization.

MEEHANITE GB300

Alloy Digest ◽  
2020 ◽  
Vol 69 (11) ◽  
Keyword(s):  
Thermal Conductivity ◽  
Tensile Strength ◽  
Compressive Strength ◽  
Gray Cast Iron ◽  
High Strength ◽  
Heat Treating ◽  
Spheroidal Graphite ◽  
Cast Irons ◽  
Test Pieces ◽  
Temperature Performance

Abstract Meehanite GB300 is a pearlitic gray cast iron that has a minimum tensile strength of 300 MPa (44 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. This grade exhibits high strength while still maintaining good thermal conductivity and good machinability. It is generally used for applications where the thermal conductivity requirements preclude the use of other higher-strength materials, such as spheroidal graphite cast irons, which have inferior thermal properties. This datasheet provides information on physical properties, hardness, tensile properties, and compressive strength as well as fatigue. It also includes information on low and high temperature performance as well as heat treating, machining, and joining. Filing Code: CI-75. Producer or source: Meehanite Metal Corporation.

MEEHANITE GA350

Alloy Digest ◽  
2020 ◽  
Vol 69 (8) ◽  
Keyword(s):  
Thermal Conductivity ◽  
Thermal Properties ◽  
Cast Iron ◽  
High Temperature ◽  
Gray Cast Iron ◽  
High Strength ◽  
Heat Treating ◽  
Spheroidal Graphite ◽  
Cast Irons ◽  
Temperature Performance

Abstract Meehanite GA350 is a heat-treatable, pearlitic gray cast iron that exhibits high strength while still maintaining good thermal conductivity and good machinability. It is generally used for applications where the thermal conductivity requirements preclude the use of other higher-strength materials such as spheroidal graphite cast irons, which have inferior thermal properties. This datasheet provides information on physical properties, hardness, elasticity, and tensile properties as well as fatigue. It also includes information on high temperature performance as well as casting, heat treating, machining, and joining. Filing Code: CI-72. Producer or Source: Meehanite Metal Corporation.

ISO 185/JL/250

Alloy Digest ◽  
2020 ◽  
Vol 69 (12) ◽  
Keyword(s):  
Thermal Conductivity ◽  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
Heat Treating ◽  
Gray Cast ◽  
Damping Capacity ◽  
Lower Strength ◽  
Test Pieces ◽  
Lower Carbon

Abstract ISO 185/JL/250 is an intermediate-tensile-strength gray cast iron that has a pearlitic matrix and a tensile strength of 250–350 MPa (36–51 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. Compared with the lower strength gray cast iron grades, ISO 185/JL/250 contains lower carbon and silicon contents and has superior wear resistance, while still maintaining good thermal conductivity, damping capacity, and machinability. This datasheet provides information on composition, physical properties, and tensile properties as well as fatigue. It also includes information on casting and heat treating. Filing Code: CI-76. Producer or source: ISO Central Secretariat.

ISO 185/JL/225

Alloy Digest ◽  
2020 ◽  
Vol 69 (9) ◽  
Keyword(s):  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
Heat Treating ◽  
International Organization ◽  
Gray Cast ◽  
Damping Capacity ◽  
Lower Strength ◽  
Test Pieces ◽  
Lower Carbon

Abstract ISO 185/JL/225 is an intermediate-tensile-strength gray cast iron that has a predominantly pearlitic matrix, and a tensile strength of 225–325 MPa (33-47 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. Compared with the lower strength gray cast iron grades, ISO 185/JL/225 contains lower carbon and silicon contents, while still maintaining excellent thermal conductivity, damping capacity, and machinability. This datasheet provides information on composition, physical properties, tensile properties, and compressive strength as well as fatigue. It also includes information on heat treating. Filing Code: CI-73. Producer or source: International Organization for Standardization (ISO).

MEEHANITE GC275

Alloy Digest ◽  
2021 ◽  
Vol 70 (2) ◽  
Keyword(s):  
Tensile Strength ◽  
Cast Iron ◽  
Physical Properties ◽  
Tensile Properties ◽  
Gray Cast Iron ◽  
Heat Treating ◽  
Gray Cast ◽  
Strength Grade ◽  
Test Pieces

Abstract Meehanite GC275 is a pearlitic gray cast iron that has a minimum tensile strength of 275 MPa (40 ksi) when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter, test bars. This intermediate-tensile-strength grade has a fine, close-grained structure that is ideal for finishing cuts. It is used for a wide variety of applications on account of its useful combination of good all round properties with adaptability to production of small and large volumes. This datasheet provides information on physical properties, hardness, and tensile properties as well as fatigue. It also includes information on heat treating, machining, and joining. Filing Code: CI-78. Producer or source: Meehanite Metal Corporation.

ISO 185/JL/275

Alloy Digest ◽  
2021 ◽  
Vol 70 (3) ◽  
Keyword(s):  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
Heat Treating ◽  
Gray Cast ◽  
Damping Capacity ◽  
Wear Properties ◽  
Lower Strength ◽  
Test Pieces ◽  
Lower Carbon

Abstract ISO 185/JL/275 is an intermediate-tensile-strength gray cast iron that has a pearlitic matrix and a tensile strength of 275–375 MPa (40–54 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. Compared with the lower strength gray cast iron grades, ISO 185/JL/275 contains lower carbon and silicon contents, while still maintaining good thermal conductivity and damping capacity. Owing to its higher tensile strength and hardness, it exhibits superior wear properties. This datasheet provides information on composition, physical properties, elasticity, tensile properties, and bend strength as well as fatigue. It also includes information on casting and heat treating. Filing Code: CI-79. Producer or source: International Organization for Standardization.

MEEHANITE GE225

Alloy Digest ◽  
2021 ◽  
Vol 70 (8) ◽  
Keyword(s):  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
Heat Treating ◽  
Gray Cast ◽  
Damping Capacity ◽  
Lower Strength ◽  
Test Pieces ◽  
Temperature Performance ◽  
Lower Carbon

Abstract Meehanite GE225 is an intermediate-tensile-strength gray cast iron that has a predominantly pearlitic matrix and a minimum tensile strength of 225 MPa (33 ksi), when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. Compared with the lower strength gray cast iron grades, Meehanite GE225 contains lower carbon and silicon contents, while still maintaining excellent thermal conductivity, damping capacity and machinability. This datasheet provides information on composition, physical properties, hardness, and tensile properties. It also includes information on high temperature performance as well as casting, heat treating, machining, and joining. Filing Code: CI-84. Producer or source: Meehanite Metal Corporation.

ISO 185/JL/200

Alloy Digest ◽  
2020 ◽  
Vol 69 (6) ◽  
Keyword(s):  
Tensile Strength ◽  
Cast Iron ◽  
Gray Cast Iron ◽  
Heat Treating ◽  
International Organization ◽  
Gray Cast ◽  
Damping Capacity ◽  
Lower Strength ◽  
Test Pieces ◽  
Lower Carbon

Abstract ISO 185/JL/200 is an intermediate-tensile-strength gray cast iron that has a predominantly pearlitic matrix, and a tensile strength of 200–300 MPa (29–44 ksi) when determined on test pieces machined from separately cast, 30 mm (1.2 in.) diameter test bars. Compared with the lower strength gray cast iron grades, 185/JL/200 contains lower carbon and silicon contents, while still maintaining excellent thermal conductivity, damping capacity, and machinability. This datasheet provides information on composition, physical properties, tensile properties, compressive and bend strength as well as fatigue. It also includes information on casting and heat treating. Filing Code: CI-70. Producer or source: International Organization for Standardization.

scholarly journals Fabrication of High-Strength Gray Cast Iron Using Permanent Magnet Scrap

2017 ◽  
Vol 62 (2) ◽  
pp. 1113-1117
Author(s):  
Seung-Yeon Park ◽  
J.H. Kim ◽  
S.J. Seo ◽  
J.S. On ◽  
K.M. Lim
Keyword(s):  
Tensile Strength ◽  
Cast Iron ◽  
Permanent Magnet ◽  
High Performance ◽  
Gray Cast Iron ◽  
High Strength ◽  
Cost Effective ◽  
Gray Cast ◽  
Cast Irons ◽  
Cast Specimen

AbstractIn this study, we have developed the manufacturing technology for high strength gray cast irons by using the spent permanent magnet scraps. The cast specimen inoculated by using a spent magnet scraps showed the excellent tensile strength up to 306MPa. This tensile strength value is 50MPa higher than that of the specimen cast without inoculation, and is similar to that of the specimen inoculated by using the expensive misch-metal. These superior mechanical properties are attributed to complex sulfides created during solidification that promote the formation and growth of Type-A graphite. It is therefore concluded that spent magnets scrap can provide an efficient and cost-effective inoculation agent for the fabrication of high-performance gray cast iron.