In this work, the effect of aluminum back surface field formed by screen printed various amount of Al paste on the effective rear surface recombination velocity (Seff) and the internal rear reflectance coeffeicient (Rb) of commercial mono-silicon solar cells was investigated. We demonstrated the effect of Seffand Rbon the performance of Al-BSF solar cells by simulating them with PC1D. The simulated results showed that the lower Seffcould get higher open circuit voltage (Voc), at the same time, the larger Rbcould get higher short-circuit current (Isc). Experimentally, we investigated the Seffand Rbthrough depositing Al paste with various amount (3.7, 5, 6, and 8 mg/cm2) for fabricating Al-BSF mono-silicon solar cells. Four group cells were characterized by light I-V, spectral response, hemispherical reflectance and scanning electron microscope (SEM) measurements. It was found that, a minimum Seffof 350 cm/s was gotten from the cells with Al paste of 8 mg/cm2, which was extracted by matching quantum efficiency (QE) from 800 nm to 1200 nm with PC1D, and a maximum Rbof 53.5% was obtained from Al paste of 5 mg/cm2by calculating at 1105 nm with PC1D. When the amount of Al paste was higher than 5mg/cm2, there were less Seffand lower Rb. On the other hand, when Al amount was 3.7mg/cm2, it was too little to form a closed BSF. Based on the SEM graphs and simulations with PC1D, a simple explaination was proposed for the experimental results.
Electrospun PVA Polymer Embedded with Ceria Nanoparticles as Silicon Solar Cells Rear Surface Coaters for Efficiency Improvement