SUMMARY
Objective:
This study evaluated the shear bond strength (SBS) of pretreated monolithic zirconia surfaces bonded to human dentin following immediate dentin sealing (IDS) using two different self-adhesive resin luting agents.
Methods and Materials:
Sixty intact human third molars were collected, stored, sectioned appropriately, and molded according to ISO 29022:2013, resulting in 120 dentin specimens. Ceramic cylindrical specimens were fabricated using CAD/CAM technology and sintered as recommended (final bonding area A=2.56 mm2). Specimens were randomly assigned to eight groups (15≥n≥14) depending on dentin conditioning method (IDS or delayed dentin sealing [DDS]), zirconia surface pretreatment (airborne particle abrasion [APA] with 50 μm Al2O3 particles at 3 bar for 10 seconds or tribochemical silica coating [TBC] with 30 μm CoJet particles at 2.8 bar for 10 seconds), and adhesive luting agent type (Panavia F2.0 [PAN] or PermaCem Dual Smartmix [PER]). Bonded specimens were water-stored (37°C, 24 hours) and subjected to SBS testing (50-kgF load cell, 1 mm/min). Fracture type was evaluated with stereomicroscopy. Data (MPa) were statistically analyzed using three-way analysis of variance (α=0.05).
Results:
All factors significantly affected SBS values (p<0.001). Dentin conditioning method presented the greatest effect. Mean SBS values ranged from 12.603 MPa (PER-APA-DDS) to 40.704 MPa (PER-TBC-IDS). Based on the fracture type, adhesive failures at the luting agent–zirconia interface were the least common.
Conclusion:
Bonding strategies for monolithic zirconia restorations could potentially benefit from IDS, regardless of the adhesive luting agent system used.
Phosphate group adsorption capacity of inorganic elements affects bond strength between CAD/CAM composite block and luting agent