Fracture Analysis of Welded Steel Connections in Pre-Crack Condition

2015 ◽  
Vol 744-746 ◽  
pp. 152-156
Author(s):  
Yu Cai Feng ◽  
Yu Ping Sun ◽  
Ju Tao Zhang ◽  
Shan Shan Yu
Keyword(s):  
Finite Element Method ◽  
Finite Element ◽  
Crack Extension ◽  
Extended Finite Element Method ◽  
Initial Crack ◽  
Extended Finite Element ◽  
Concentrated Load ◽  
Weld Root ◽  
Crack Condition ◽  
Element Method

Extended finite element method (XFEM) can effectively describe the phenomenon of steel node cracks growth and extension. In this paper, extended finite element method is used for the beam weld node end under the concentrated load to analyze node fracture under no initial crack and pre-crack condition. The result shows that: under the no initial crack condition, crack appears near the weld root, where the bottom and upper of the weld is easy to crack than the middle,because of the necking phenomenon,which means that both end stress is higher than the middle. Crack firstly appears in the weld bottom, extending from the bottom to up. The crack tip makes stress concentration, which accelerates the crack extension. The location of the pre-crack has the influence on the node fracture, which means that the farther the position from the weld root is, the harder it is to crack and grow. Pre-crack position coincides with no initial crack extension path, promoting crack growth and extension.

Numerical Analysis of API 5L X42 and X52 Vintage Pipes with Cracks in Corrosion Defects Using Extended Finite Element Method

2021 ◽  
Author(s):  
Xinfang Zhang ◽  
Meng Lin ◽  
Allan Okodi ◽  
Leichuan Tan ◽  
Juliana Leung ◽  
...  
Keyword(s):  
Finite Element Method ◽  
Finite Element ◽  
Extended Finite Element Method ◽  
Pipe Wall ◽  
Crack Depth ◽  
Initial Crack ◽  
Extended Finite Element ◽  
Failure Pressure ◽  
Corrosion Defects ◽  
Element Method

Abstract Cracks and corrosion in pipelines can occur simultaneously, representing a hybrid defect known as cracks in corrosion (CIC), which is often difficult to model using the available assessment codes or methods. As a result, detailed modeling of CIC has not been studied extensively. In this study, the extended finite element method (XFEM) has been applied to predict the failure pressures of CIC defects in API 5L Grade X42 and X52 pipes. The pipes were only subjected to internal pressure and the XFEM models were validated using full-scale burst tests available in the literature. Several CIC models with constant total defect depths (55%, and 60% of wall thickness) were constructed to investigate the effect of the initial crack depth on the failure pressure. The failure criterion was defined when wall penetration occurred due to crack growth, i.e., the instance the crack reached the innermost element of the pipe wall mesh. It was observed that for shorter cracks, the failure pressure decreased with the increase of the initial crack depth. The results indicated that the CIC defect could be treated as crack-only defects when the initial crack depth exceeded 50% of the total defect depth. However, for longer cracks, the initial crack depth was found to have a negligible effect on the failure pressure, implying that the CIC defect could be treated as either a crack or a corrosion utilizing the available assessment methods.

scholarly journals A mesh-independent framework for crack tracking in elastodamaging materials through the regularized extended finite element method

2021 ◽  
Author(s):  
Elena Benvenuti ◽  
Nicola Orlando
Keyword(s):  
Finite Element Method ◽  
Finite Element ◽  
Damage Evolution ◽  
Extended Finite Element Method ◽  
Mesh Adaptivity ◽  
Extended Finite Element ◽  
Evolution Law ◽  
Crack Paths ◽  
Original Crack ◽  
Element Method

AbstractWe propose a formulation for tracking general crack paths in elastodamaging materials without mesh adaptivity and broadening of the damage band. The idea is to treat in a unified way both the damaging process and the development of displacement discontinuities by means of the regularized finite element method. With respect to previous authors’ contributions, a novel damage evolution law and an original crack tracking framework are proposed. We face the issue of mesh objectivity through several two-dimensional tests, obtaining smooth crack paths and reliable structural results.

scholarly journals An Extended Finite Element Method (XFEM) Study on the Elastic T-Stress Evaluations for a Notch in a Pipe Steel Exposed to Internal Pressure

Mathematics ◽  
2021 ◽  
Vol 9 (5) ◽  
pp. 507
Author(s):  
K. Yakoubi ◽  
S. Montassir ◽  
Hassane Moustabchir ◽  
A. Elkhalfi ◽  
Catalin Iulian Pruncu ◽  
...  
Keyword(s):  
Finite Element Method ◽  
Finite Element ◽  
Internal Pressure ◽  
Extended Finite Element Method ◽  
Research Study ◽  
Extended Finite Element ◽  
T Stress ◽  
Cracked Structures ◽  
Element Method

The work investigates the importance of the K-T approach in the modelling of pressure cracked structures. T-stress is the constant in the second term of the Williams expression; it is often negligible, but recent literature has shown that there are cases where T-stress plays the role of opening the crack, also T-stress improves elastic modeling at the point of crack. In this research study, the most important effects of the T-stress are collected and analyzed. A numerical analysis was carried out by the extended finite element method (X-FEM) to analyze T-stress in an arc with external notch under internal pressure. The different stress method (SDM) is employed to calculate T-stress. Moreover, the influence of the geometry of the notch on the biaxiality is also examined. The biaxiality gave us a view on the initiation of the crack. The results are extended with a comparison to previous literature to validate the promising investigations.

Sign in / Sign up

Export Citation Format

Share Document