Design of Magnesia–Spinel Bricks for Improved Coating Adherence in Cement Rotary Kilns

It is well known that doloma bricks present better coating adherence than magnesia–spinel bricks when applied in cement rotary kilns, which is related to the different coating formation mechanism. The coating has an essential role in prolonged operation by protecting the refractory lining; thus, it is important to improve its adherence on magnesia–spinel refractories. The objective of this investigation is to study different compositions of magnesia–spinel bricks, achieved by varying additives used (calcined alumina, limestone, hematite and zirconia) and firing temperature (1500 °C and 1700 °C), to enhance the coating adherence measured by the sandwich test. The results have pointed out that the use of higher firing temperature contributes positively to physical adherence due to well-sintered refractory structure and elevated permeability, attaining coating strength superior to 2 MPa. For the chemical adherence, the addition of 2 wt.% of limestone increased the coating strength to 3 MPa, but resulted in a drop in hot properties. In this context, the most suitable approach to improve adherence of clinker coating and maintain hot properties in suitable levels is to increase the firing temperature.

Researches on development of alumina-chromia-zirconium silicate refractories containing 60 % Cr2O3

Researches of a branch composition and firing atmosphere influence on structure and properties of pressed alumina-chromia-zirconium silicate refractories with 60 % Cr2O3 content were carried out. The optimal branch composition which after firing in oxidizing atmosphere provides obtaining of samples with open porosity 24.8 %, apparent density 3.46 g/cm3, cold crushing strength 78 N/mm2 and thermal shock resistance by 950 ºС — water — 7 thermal cycles was established. The phase composition of samples was determined. It has been shown that, firing in a reducing atmosphere, as well as titanium oxide addition, have no significant effect on samples properties. Corrosion resistance comparative researches of alumina-chromia-zirconium silicate refractories with 60 % Cr2O3 content and refractory brand KHTSS-30 with 30 % Cr2O3 content to glass «E» and basalt melts by crucible method at a temperature of 1580 °C with an exposure time of 8 hours were carried out. It has been established that, glass «E» and basalt impregnate refractories, moreover for samples with the developed optimal composition the impregnation depth was the smallest in comparison with samples of other compositions. The corrosion mechanism has been established, which consists in the penetration of glass «E» and basalt melts into refractory with further dissolution of corundum grains in them. Sintered Cr2O3 and solid solutions based on it in the composition of samples prevent corrosion, reducing the interaction area of melts with corundum grains, and when exposed to basalt melt, also forming spinelid with its components, which slows down further penetration of melt into refractory structure, thereby reducing its corrosive effect on the refractory. Based on the obtained results, a technology of a new domestic type of product (alumina-chromia-zirconium silicate refractories with 60 % Cr2O3 content manufactured by semi-dry pressing method) was developed.

Development and Application on Large Annular Shaft Kiln at Shougang

The current status of technical development of annular shaft kiln for limestone calcination production is described in this paper. Based on the existing technological accumulation, a new type annular shaft kiln with capacity of 600t/d has been developed independently by Beijing Shougang International Engineering Technology Co. Ltd. A number of key technologies of the new type large annular shaft kiln are researched and integrated, include thermal process system determination, lining refractory structure optimization, heat-exchanger configuration etc. The major advanced characteristics of new type annular shaft kiln are energy saving, higher efficiency, lower environmental pollution, lower emission, lower engineering investment, and lower operation cost. The excellent performances and application results in production have been achieved at Shougang Qiangang steel plant.