EPR Study of the Mn-Doped Magnesium Titanate Ceramics

Manganese-doped magnesium titanate ceramic samples obtained by a solid-state reaction via sintering in the air from a mixture of MgO and TiO2 powders of different molar ratios were analyzed by electron paramagnetic resonance (EPR) technique. The EPR signals of Mn2+ ions (S = 5/2, І = 5/2) in crystal phases of MgO, Mg2TiO4, and MgTiO3 were detected. We have obtained the following spin Hamiltonian parameters for Mn2+ ions: g = 2.0015, A ~ 81 ∗ 10-4 cm-1 (in MgO phase); g = 2.0029, A ~ 73.8 ∗ 10-4 cm-1, b2 0 = 35 ∗ 10-4 cm-1 (in Mg2TiO4 phase); g = 2.004, A ~ 79 ∗ 10-4 cm-1, b2 0 = 165 ∗ 10-4 cm-1 (in MgTiO3 phase). Despite the presence of Mn4+ centers in both Mg2TiO4:Mn and MgTiO3:Mn ceramics confirmed by previous optical studies, no EPR signals related to Mn4+ ions (S = 3/2, І = 5/2) were found. The Mn2+ EPR signals are proposed as structural probes in manganese-doped magnesium titanate ceramics.

OPTIMIZATION OF TECHNOLOGY FOR PRODUCING A COMPOSITE BASED ON BARIUM FERRITE AND BARIUM TITANATE

В работе показано, что в результате спекания образцов композита титанат бария (80 объемных %) - феррит бария (20 объемных %) в фарфоровом тигле при температуре 1300 °С возникает эвтектика. В результате сравнения свойств образцов, полученных при различных температурах спекания, установлено, что оптимальные свойства имеют образцы, спеченные при 1250 °С. Проведено сравнение структуры и диэлектрических свойств образцов керамики титаната бария и композита титанат бария (80 объемных %) - феррит бария (20 объемных %), спеченных при температуре 1250°С. Показано, что добавление в состав титаната бария 20% феррита бария повышает значение диэлектрической проницаемости, пироэлектрического коэффициента и пьезоэлектрического модуля d композита в 1,5 - 2 раза по сравнению с керамикой титаната бария, тогда как значение пьезоэлектрического модуля d остается без изменения. Введение в состав керамики титаната бария 20 % феррита бария достаточно для того, чтобы полученный композит имел магнитные характеристики, соответствующий чистому ферриту бария. It is shown in the work that as a result of sintering of composite samples of barium titanate (80 vol. %) - barium ferrite (20 vol. %) in a porcelain crucible at a temperature of 1300 °C, a eutectic appears. As a result of comparing the properties of the samples obtained at different sintering temperatures, it was found that the samples sintered at 1250 °C have optimal properties. The structure and dielectric properties of barium titanate ceramic samples and barium titanate (80 vol. %) - barium ferrite (20 vol. %) composite sintered at a temperature of 1250 °C are compared. It has been shown that the addition of 20% barium ferrite to the composition of barium titanate increases the dielectric constant, pyroelectric coefficient, and piezoelectric modulus d of the composite of 1,5 - 2 times compared to barium titanate ceramics, while the value of the piezoelectric modulus d remains unchanged. The introduction of 20 % barium ferrite into the barium titanate ceramics is sufficient for the resulting composite to have magnetic characteristics corresponding to pure barium ferrite.

Novel yellow to blackish green Ni-doped aluminium titanate ceramic pigments

Novel yellow to blackish green Ni-doped aluminium titanate (Al2TiO5) ceramic pigments were synthesized by solid-state reaction method at 1400 ?C. Effects of nickel doping content on phase composition, microstructure, optical properties and stability were studied. The results show that the higher content of Al2TiO5 phase and the reduction of the lattice distortion of aluminium titanate could be attributed to the entry of nickel ions into aluminium titanate lattice resulting in the formation of solid solution. Ni-doped aluminium titanate ceramic pigments show exceptional glaze colouring and are expected to be promising high-temperature pigments.