Microstructure and Mechanical Properties of TA15 Alloy Produced by Electron Beam Melting

2021 ◽  
Author(s):  
Jiangtao Ran ◽  
Fengchun Jiang ◽  
Zhuo Chen ◽  
Hong Zhao
Keyword(s):  
Mechanical Properties ◽  
Electron Beam ◽  
Electron Beam Melting ◽  
Microstructure And Mechanical Properties ◽  
Ta15 Alloy

scholarly journals Tailoring Microstructure and Mechanical Properties of Additively-Manufactured Ti6Al4V Using Post Processing

Materials ◽  
2021 ◽  
Vol 14 (3) ◽  
pp. 658
Author(s):  
Yaron Itay Ganor ◽  
Eitan Tiferet ◽  
Sven C. Vogel ◽  
Donald W. Brown ◽  
Michael Chonin ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Electron Beam ◽  
Fatigue Resistance ◽  
Electron Beam Melting ◽  
High Reliability ◽  
National Laboratory ◽  
Post Processing ◽  
Proof Stress ◽  
Β Phase ◽  
Microstructure And Mechanical Properties

Additively-manufactured Ti-6Al-4V (Ti64) exhibits high strength but in some cases inferior elongation to those of conventionally manufactured materials. Post-processing of additively manufactured Ti64 components is investigated to modify the mechanical properties for specific applications while still utilizing the benefits of the additive manufacturing process. The mechanical properties and fatigue resistance of Ti64 samples made by electron beam melting were tested in the as-built state. Several heat treatments (up to 1000 °C) were performed to study their effect on the microstructure and mechanical properties. Phase content during heating was tested with high reliability by neutron diffraction at Los Alamos National Laboratory. Two different hot isostatic pressings (HIP) cycles were tested, one at low temperature (780 °C), the other is at the standard temperature (920 °C). The results show that lowering the HIP holding temperature retains the fine microstructure (~1% β phase) and the 0.2% proof stress of the as-built samples (1038 MPa), but gives rise to higher elongation (~14%) and better fatigue life. The material subjected to a higher HIP temperature had a coarser microstructure, more residual β phase (~2% difference), displayed slightly lower Vickers hardness (~15 HV10N), 0.2% proof stress (~60 MPa) and ultimate stresses (~40 MPa) than the material HIP’ed at 780 °C, but had superior elongation (~6%) and fatigue resistance. Heat treatment at 1000 °C entirely altered the microstructure (~7% β phase), yield elongation of 13.7% but decrease the 0.2% proof-stress to 927 MPa. The results of the HIP at 780 °C imply it would be beneficial to lower the standard ASTM HIP temperature for Ti6Al4V additively manufactured by electron beam melting.

Electron beam melting of Ti–48Al–2Cr–2Nb alloy: Microstructure and mechanical properties investigation

2011 ◽  
Vol 19 (6) ◽  
pp. 776-781 ◽  
Author(s):  
S. Biamino ◽  
A. Penna ◽  
U. Ackelid ◽  
S. Sabbadini ◽  
O. Tassa ◽  
...  
Keyword(s):  
Mechanical Properties ◽  
Electron Beam ◽  
Electron Beam Melting ◽  
Microstructure And Mechanical Properties ◽  
Alloy Microstructure
Sign in / Sign up

Export Citation Format

Share Document