scholarly journals Tailoring Microstructure and Mechanical Properties of Additively-Manufactured Ti6Al4V Using Post Processing

Materials ◽  
2021 ◽  
Vol 14 (3) ◽  
pp. 658
Author(s):  
Yaron Itay Ganor ◽  
Eitan Tiferet ◽  
Sven C. Vogel ◽  
Donald W. Brown ◽  
Michael Chonin ◽  
...  

Additively-manufactured Ti-6Al-4V (Ti64) exhibits high strength but in some cases inferior elongation to those of conventionally manufactured materials. Post-processing of additively manufactured Ti64 components is investigated to modify the mechanical properties for specific applications while still utilizing the benefits of the additive manufacturing process. The mechanical properties and fatigue resistance of Ti64 samples made by electron beam melting were tested in the as-built state. Several heat treatments (up to 1000 °C) were performed to study their effect on the microstructure and mechanical properties. Phase content during heating was tested with high reliability by neutron diffraction at Los Alamos National Laboratory. Two different hot isostatic pressings (HIP) cycles were tested, one at low temperature (780 °C), the other is at the standard temperature (920 °C). The results show that lowering the HIP holding temperature retains the fine microstructure (~1% β phase) and the 0.2% proof stress of the as-built samples (1038 MPa), but gives rise to higher elongation (~14%) and better fatigue life. The material subjected to a higher HIP temperature had a coarser microstructure, more residual β phase (~2% difference), displayed slightly lower Vickers hardness (~15 HV10N), 0.2% proof stress (~60 MPa) and ultimate stresses (~40 MPa) than the material HIP’ed at 780 °C, but had superior elongation (~6%) and fatigue resistance. Heat treatment at 1000 °C entirely altered the microstructure (~7% β phase), yield elongation of 13.7% but decrease the 0.2% proof-stress to 927 MPa. The results of the HIP at 780 °C imply it would be beneficial to lower the standard ASTM HIP temperature for Ti6Al4V additively manufactured by electron beam melting.

2011 ◽  
Vol 19 (6) ◽  
pp. 776-781 ◽  
Author(s):  
S. Biamino ◽  
A. Penna ◽  
U. Ackelid ◽  
S. Sabbadini ◽  
O. Tassa ◽  
...  

Metals ◽  
2020 ◽  
Vol 10 (5) ◽  
pp. 593
Author(s):  
Changyong Liu ◽  
Zhuokeng Mai ◽  
Deng Yan ◽  
Mingguang Jiang ◽  
Yuhong Dai ◽  
...  

This study investigated the effects of hot isostatic pressing (HIP) on the microstructures and mechanical properties of Ti6Al4V fabricated by electron beam melting (EBM). The differences of surface morphologies, internal defects, relative density, microstructures, textures, mechanical properties and tensile fracture between the as-built and HIPed samples were observed using various characterization methods including optical metallography microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electron backscattered diffraction (EBSD) and tensile tests. It was found that the main effects of HIP on microstructures include—the increase of average grain size from 7.96 ± 1.21 μm to 11.34 ± 1.89 μm, the increase of α lamellar thickness from 0.71 ± 0.15 μm to 2.49 ± 1.29 μm and the increase of β phase ratio from 4.7% to 10.5% in terms of area fraction on the transversal section. The combinatorial effects including densification, increase of grain size, α lamellar thickness, β phase ratio, reduction of dislocation density and transformation of dislocation patterns contributed to the improvement of elongation and ductility of EBM-fabricated Ti6Al4V. Meanwhile, these effects also resulted in a slight reduction of the yield strength and UTS mainly due to the coarsening effect of HIP.


Sign in / Sign up

Export Citation Format

Share Document