The feasibility of using the ultrasonic melt treatment to prepare billets for thixocasting process of hypoeutectic Al-7%Si alloys was studied in this paper. The work covered the billet preparation, soaking treatments and thixocasting process, with focus on the microstructural features in each case. The results showed that the use of ultrasonic treatment in billet preparation resulted in highly uniform, fine and non-dendritic microstructures. Billets with globule sizes as small as 58 µm, and roundness of more than 0.7 were obtained by ultrasonic melt treatment. Different soaking conditions before thixocasting were done and the optimum from which was the soaking for 5 min at 580°C, which resulted in thixocast parts with excellent combination of fine globules of 80 µm and roundness of 0.7 - 0.81. The eutectic Si, as well, was greatly refined by the ultrasonic thixocasting process. Furthermore, high-Fe ultrasonic treated billets, which were thixocasted successfully, exhibited Fe-intermetallic particles in highly desirable fine compacted form. These results reveal the feasibility and competence of UST as a potential route for feedstock production.
Correction to: The Microstructure Refinement and Strength Enhancement of Mg–Al–Si Alloy Subjected by Alternating-Frequency Ultrasonic Melt Treatment