Characterizing the Effect of Processing Parameters on Temperature Distribution of 7075 Aluminum Alloy Slurry Prepared by Enthalpy Control Process

There is a strong demand for high-strength aluminum alloys such as 7075 aluminum alloy to be applied for rheocasting industry. The overriding challenge for the application of 7075 alloy is that its solid fraction is very sensitive to the variation of temperature in the range of 40% ~ 50% solid fraction, which inevitably narrows down the processing window of slurry preparation for rheocasting process. Therefore, in this work, a novel method to prepare semi-solid slurry of the 7075 alloy, so called Enthalpy Control Process (ECP), has been developed to grapple with this issue. In the method, a medium-frequency electromagnetic field was applied on the outside of slurry preparation crucible to reduce the temperature difference throughout the slurry. The effect of processing parameters, including heating power, heating time, the initial temperature of crucible and melt weight, on the temperature field of the semi-solid slurry was investigated. The results exhibited that although the all the processing parameters had a great influence on the average temperature of the slurry, heating time was the main factor affecting the maximum temperature difference of the slurry. The optimum processing parameters during ECP were found to be heating power of 7.5 KW, the initial temperature of crucible of 30 °C ~ 200 °C and melt weight of 2 kg.

Warm sheet metal forming of energy-absorbing elements made 7075 aluminum alloy in the hardened state T6

The article covers experimental research on the forming of products made of 7075 aluminum alloy. This aluminum alloy grade is characterized by high strength, but due to its low formability in T6 temper, its use in the stamping processes of complex structural elements is limited. The authors have manufactured a U-shaped element at an elevated temperature and determined the optimal parameters of the process. Conventional heating of the sheet and shaping it at the temperature of 100 and 150 °C allowed to obtain a product of high strength similar to the T6 state, above 540 MPa. Due to the excessive springback of the sheet during forming, these products were characterized by a large deviation of the shape geometry, exceeding the allowable values of + / − 1 mm. Only the use of an alternative method of heating the sheet to temperatures of 200 and 240 °C (between plates at 350 °C, heating time 2 min, heating rate 1.8 °C/s) allowed to obtain a product that meets both the strength and geometric requirements. The determined optimal process’ parameters were later transferred to the stamping process of elements of a more complex shape (lower part of the B-pillar). The sheet was heated up and formed in the previously pre-heated tools. In the subsequent series of tests, the heating method and the blank’s temperature were being analyzed. In the case of the foot of the B-pillar, it was necessary to lower the initial blank temperature to 200 °C (heating in a furnace with a temperature of 340 °C, heating speed 0.5 °C/s). The appropriate combination of the process parameters resulted in the satisfactory shape deviation and reaching the product’s strength comparable to the strength of the material in as-delivered T6 temper. Using electron microscopy, it was verified that the structure of the finished product contained particles MgZn2 that strongly strengthen the alloy. The obtained results complement the data on the possibility of using 7075 aluminum alloy to produce energy-absorbing elements of motor vehicles.

Effects of polyvinylidene fluoride sealing on micro-arc oxidation coating of 7075 aluminum alloy

Purpose The purpose of this is to study the effects of organic sealing on the structure and performance of the micro-arc oxidation (MAO) film of 7075 aluminum alloy. Design/methodology/approach The 7075 aluminum alloy was treated by micro-arc oxidation technology, then the MAO films were sealed by polyvinylidene fluoride (PVDF) solutions with different concentrations to forms a MAO/PVDF composite coating on the surface of the 7075 aluminum alloy matrix. Findings The results show that the MAO/PVDF film thickness increased to 24.8 um. When the PVDF concentration was 8 g/L, and the sealed film reached best corrosion resistance and wear resistance. Originality/value The effects of different concentrations of PVDF on microarc oxidation properties of 7075 aluminum alloy were studied.