Laser metal deposition (LMD) is an advanced technology of additive manufacturing which involves sophisticated processes. However, it is associated with high risks of failure due to the possible generation of cracks and bubbles. If not identified in time, such defects can cause substantial losses. In this paper, real-time monitoring of LMD samples and online detection of cracks by an infrared monochrome pyrometer (IMP) could mitigate this risk. An experimental platform for crack detection in LMD samples was developed, and the identification of four simulated cracks in a 316L austenitic stainless-steel LMD sample was conducted. Data at temperatures higher than 150 °C were collected by an IMP, and the results indicated that crack depth is an important factor affecting the peak temperature. Based on this factor, the locations of cracks in LMD-316L austenitic stainless-steel samples can be determined. The proposed technique can provide real-time detection of cracks through layers of cladding during large-scale manufacturing, which suggests its relevance for optimizing the technological process and parameters, as well as reducing the possibility of cracks in the LMD process.
Crack Detection during Laser Metal Deposition by Infrared Monochrome Pyrometer