Carbon dioxide CO2could corrode the oil well cement paste matrix under agreeable moisture and pressure condition in deep oil wells, which could decrease the compressive strength and damage the annular seal reliability of cement paste matrix. The problem of oil well cement paste matrix corrosion by CO2was researched in the paper for obtain the feasible corrosion prevention technical measures. The microstructure and compressive strength of corroded cement paste matrix were examined by scanning electron microscopeSEMand strength test instrument etc. under different corrosion conditions. The mechanism and effect law of corrosion on oil well cement paste matrix by CO2were analyzed. And the suitable method to protect CO2corrosion in deep oil wells was explored. The results show that the corrosion mechanism of cement paste matrix by CO2was that the wetting phase CO2could generate chemical reaction with original hydration products produced from cement hydration, which CaCO3were developed and the original composition and microstructure of cement paste matrix were destroyed. The compressive strength of corrosion cement paste matrix always was lower than that of un-corrosion cement paste matrix. The compressive strength of corrosion cement paste matrix decreased with increase of curing temperature and differential pressure. The corroded degree of cement paste matrix was intimately related with the compositions of cement slurry. Developing and design anti-corrosive cement slurry should base on effectively improving the compact degree and original strength of cement paste matrix. The compounding additive R designed in the paper could effectively improve the anti-corrosive ability of cement slurry.
Effects of confinement pressure on the mechanical behavior of an oil well cement paste