Effects of Heat Treatment and Nitrogen on Microstructure and Mechanical Properties of 1Cr12NiMo Martensitic Stainless Steel

2012 ◽  
Vol 28 (11) ◽  
pp. 1059-1066 ◽  
Author(s):  
Ruicheng Fan ◽  
Ming Gao ◽  
Yingche Ma ◽  
Xiangdong Zha ◽  
Xianchao Hao ◽  
...  
Metals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 392
Author(s):  
Jaka Burja ◽  
Blaž Šuler ◽  
Marko Češnjaj ◽  
Aleš Nagode

Standard heat treatment of martensitic stainless steel consists of quenching and tempering. However, this results in high strength and hardness, while Charpy impact toughness shows lower values and a large deviation in its values. Therefore, a modified heat treatment of 0.1C-13Cr-3Ni martensitic stainless steel (PK993/1CH13N3) with intercritical annealing between Ac1 and Ac3 was introduced before tempering to study its effect on the microstructure and mechanical properties (yield strength, tensile strength, hardness and Charpy impact toughness). The temperatures of intercritical annealing were 740, 760, 780 and 800 °C. ThermoCalc was used for thermodynamic calculations. Microstructure characterization was performed on an optical and scanning electron microscope, while XRD was used for the determination of retained austenite. Results show that intercritical annealing improves impact toughness and lowers deviation of its values. This can be attributed to the dissolution of the thin carbide film along prior austenite grain boundaries and prevention of its re-occurrence during tempering. On the other hand, lower carbon concentration in martensite that was quenching from the intercritical region resulted in lower strength and hardness. Intercritical annealing refines the martensitic microstructure creating a lamellar morphology.


IARJSET ◽  
2016 ◽  
Vol 3 (4) ◽  
pp. 6-12 ◽  
Author(s):  
Johnpaul C Ezechidelu ◽  
Samuel O Enibe ◽  
Daniel O Obikwelu ◽  
Paul S Nnamchi ◽  
Camillus S Obayi

2020 ◽  
Vol 2020 ◽  
pp. 1-16
Author(s):  
Sheida Sarafan ◽  
Priti Wanjara ◽  
Jean-Benoît Lévesque ◽  
Javad Gholipour ◽  
Henri Champliaud ◽  
...  

In this study, the integrity of electron beam- (EB-) welded CA6NM—a grade of 13% Cr-4% Ni martensitic stainless steel—was assessed through the entire joint thickness of 90 mm after postweld heat treatment (PWHT). The joints were characterized by examining the microstructure, residual stresses, global mechanical properties (static tensile, Charpy impact, and bend), and local properties (yield strength and strain at fracture) in the metallurgically modified regions of the EB welds. The applied PWHT tempered the “fresh” martensite present in the microstructure after welding, which reduced sufficiently the hardness (<280 HV) and residual stresses (<100 MPa) to meet the requirements for hydroelectric turbine assemblies. Also, the properties of the EB joints after PWHT passed the minimum acceptance criteria specified in ASME sections VIII and IX. Specifically, measurement of the global tensile properties indicated that the tensile strengths of the EB welds in the transverse and longitudinal directions were on the same order as that of the base metal (BM). Evaluation of the local tensile properties using a digital image correlation (DIC) methodology showed higher local yield strengths in the fusion zone (FZ) and heat-affected zone (HAZ) of 727 MPa and 740 MPa, respectively, relative to the BM value of 663 MPa. Also, the average impact energies for the FZ and HAZ were 63 J and 148 J, respectively, and attributed to the different failure mechanisms in the HAZ (dimples) versus the FZ (quasi-cleavage consisting of facets and dimples). This study shows that the application of PWHT plays an important role in improving the weld quality and performance of EB-welded CA6NM and provides the essential data for validating the design and manufacturing process for next-generation hydroelectric turbine products.