Strengthening Mechanism and Carbide Precipitation Behavior of Nb-Mo Microalloy Medium Mn Steel

This study investigates the strengthening mechanism and carbide precipitation behavior of medium Mn steel with Nb-Mo microalloy after cyclic quenching and austenite reverse transformation treatment. The results show that the Nb/Mo element not only precipitates (Nb,Mo)C in the grains, hindering the movement of dislocations and increases the strength, but also segregates at the austenite/ferrite grain boundary, thus delaying the transformation from austenite to ferrite. In addition, a large amount of nano-scale cementite is retained after cyclic quenching and austenite reverse transformation, which has a positive effect on the proportion of retained austenite in medium Mn steel. Moreover, the carbides with small size and low Mn content are dissolved, and the decomposed C and Mn content are beneficial to the nucleation of austenite during the intercritical annealing process at a temperature of 690 °C.

Microstructure Evolution and Tensile Behaviour of a Cold Rolled 8 Wt Pct Mn Medium Manganese Steel

A novel medium manganese steel with composition Fe–8.3Mn–3.8Al–1.8Si–0.5C–0.06V–0.05Sn was developed and thermomechanically processed through hot rolling and intercritical annealing. The steel possessed a yield strength of 1 GPa, tensile strength of 1.13 GPa and ductility of 41 pct. In order to study the effect of cold rolling after intercritical annealing on subsequent tensile properties, the steel was further cold rolled up to 20 pct reduction. After cold rolling, it was observed that the strain hardening rate increased continuously with increasing cold rolling reduction but without a significant drop in ductility during subsequent tensile tests. The microstructural evolution with cold rolling reduction was analysed to understand the mechanisms behind this phenomena. It was found that cold rolling activated additional twinning systems which provided a large number of potent nucleation sites for strain induced martensite to form during subsequent tensile tests in what can be described as an enhanced TRIP effect.

Effect of Carbon Content and Intercritical Annealing on Microstructure and Mechanical Tensile Properties in FeCMnSiCr TRIP-Assisted Steels

Four TRIP (Transformation Induced Plasticity) assisted steels, three TBF (TRIP Bainitic Ferrite) steels and one TPF (TRIP Polygonal Ferrite) steel, were manufactured from three different carbon contents (0.2, 0.3 and 0.4 wt.% C), to study the evolution of their microstructure and tensile mechanical properties in 15 mm thick plates. TBF steels were subjected to the same austenitization heat treatment and subsequent bainitization isothermal treatment. The TPF steel was subjected to an intercritical annealing and subsequent isothermal bainitization treatment. All were microstructurally characterized by optical, scanning electron and atomic force microscopy, as well as X-ray diffraction. Mechanically, they were characterized by the ASTM E8 tensile test and fractographies. For the TBF steels, the results showed that when the carbon content increased, there were an increase in volume fraction of retained austenite, of the microconstituent “martensite/retained austenite” and in the tensile strength; and a decrease in the volume fraction of bainitic ferrite matrix and elongation; with an improvement in TRIP behavior due to the increase in retained austenite. The TPF steel presented around 50% ductile polygonal ferrite developing better TRIP behavior than the TBF steels. The evolution of the fractographies was ductile to brittle for TBF steels with an increase in carbon content, and for TPF, the appearance of the fracture surface was ductile.