Dissolution, crystallization and second dissolution traces of isotactic poly(propylene) have been obtained in a slow temperature ramp (3 K h-1) with the C80 Setaram calorimeter. Traces of phase-change, in presence of solvent, are comparable to traces without solvent. The change of enthalpy on heating or cooling, ∆Htotal, over the 40-170 °C temperature range, is the sum of two contributions, ∆HDSC and ∆Hnetwork. The change ∆HDSC is the usual heat obtained in a fast temperature ramp and ∆Hnetwork is associated with a physical network whose disordering is slow and subject to superheating due to strain. When dissolution is complete, ∆Htotal is equal to ∆H0, the heat of fusion of perfect crystals. The values of ∆Htota for nascent and recrystallized samples are compared. Dissolution is the tool to evaluate the quality of the crystals. The repartition of ∆Htotal, into the two endotherms, reflects the quality of crystals. The crystals grown more rapidly have a higher fraction of network crystals which are stable at high T in the solvents. A complete dissolution, i.e. a high temperature (170 °C or more) is necessary to obtain good crystals. The effect of concentration, polymer molecular weight and solvent quality on crystal growth is analyzed.
Reinforcement of macroscopic carbon nanotube structures by polymer intercalation: The role of polymer molecular weight and chain conformation