scholarly journals Solution combustion synthesis of highly dispersible and dispersed iridium oxide as an anode catalyst in PEM water electrolysis

2017 ◽  
Vol 5 (10) ◽  
pp. 4774-4778 ◽  
Author(s):  
Muralidhar G. Chourashiya ◽  
Atsushi Urakawa
Keyword(s):  
Combustion Synthesis ◽  
Water Oxidation ◽  
Solution Combustion Synthesis ◽  
Water Electrolysis ◽  
Iridium Oxide ◽  
Anode Catalyst ◽  
Solution Combustion ◽  
Highly Dispersed ◽  
Oxidation Performance

Highly dispersed and dispersible nano-structured IrO2 made by solution combustion synthesis showed excellent water oxidation performance in PEM water electrolysis.

Solution-Combustion Synthesis and Study of : γ-Fe2-xCrxO3(0.75 ≤ x ≤ 1.25) Maghemite-like Materials

2008 ◽  
Author(s):  
Emilio Moran ◽  
Miguel ïngel. Alario-Franco ◽  
Marco L. Garcia-Guaderrama ◽  
Oscar Blanco
Keyword(s):  
Combustion Synthesis ◽  
Solution Combustion Synthesis ◽  
Solution Combustion

Effect of Nitric Acid Modification on LiMn2O4 Prepared by Solution Combustion Synthesis

2011 ◽  
Vol 80-81 ◽  
pp. 332-336 ◽  
Author(s):  
Yan Xia ◽  
Mei Huang ◽  
Jun Ming Guo ◽  
Ying Jie Zhang
Keyword(s):  
Nitric Acid ◽  
Combustion Synthesis ◽  
Discharge Capacity ◽  
Retention Rate ◽  
Solution Combustion Synthesis ◽  
Manganese Acetate ◽  
Solution Combustion ◽  
Acid Modification ◽  
Capacity Retention ◽  
Liquid Combustion

Effect of nitric acid and the burning time on the liquid combustion synthesis of spinel LiMn2O4 has been studied, using lithium nitrite and Manganese acetate as raw a material. The results show that the main phases are all LiMn2O4, which can be obtained at 400-600 oC. Before modified, the impurity is Mn3O4 or Mn2O3. After modified, the impurity is only Mn3O4. The aggregation obviously reduced after adding nitric acid, it is indicated that the crystalline increased. With the increasing temperatures, the modified particle size was increased and the aggregation reduced. The initial discharge capacity and cycle stability improved at some extent too. Its first discharge capacity was 104.6, 112.8 and 117.7mAh/g synthesized at 400, 500, 600 oC, respectively, and the 30th capacity retention rate were 84.89%, 80.67% and 73.24%.

Solution combustion synthesis and luminescence properties of (Y,Gd)Al3(BO3)4:Eu3+ phosphors

2010 ◽  
Vol 28 (5) ◽  
pp. 709-712 ◽  
Author(s):  
Guifang LI ◽  
Quanxi CAO ◽  
Zhimin LI ◽  
Yunxia HUANG ◽  
Haiqing JIANG
Keyword(s):  
Combustion Synthesis ◽  
Solution Combustion Synthesis ◽  
Luminescence Properties ◽  
Solution Combustion
Sign in / Sign up

Export Citation Format

Share Document