ABSTRACTPerovskite ferroelectric thin films in the paraelectric state exhibit outstanding dielectric properties, even at high frequencies (>1 GHz). The tunable dielectric constant of ferroelectric thin films can be used to design frequency and phase agile components. High dielectric constant thin film ferroelectric materials in the paraelectric state have received enormous attention due to their feasibility in applications such as decoupling capacitors and tunable microwave capacitors; the latter application has been fueled by the recent explosion in wireless and satellite communications. This paper reportsBa0.96Ca 0.04Ti0.84Zr0.16O3 (BCTZ) thin films that were deposited on Pt electrodes using radio frequency magnetron sputtering at a low (450 °C) substrate temperature. Sputtered thin film BCTZ at low substrate temperature is compatible with conventional integrated circuit technology. The structural characterization of the deposited films was performed by x-ray diffraction. The electrical characterization of the films was achieved by capacitance-voltage, current-voltage, and S-parameter (via vector network analyzer) measurements. In addition, the effect of post annealing on the deposited films was investigated. A detailed understanding of both their processing and material properties is discussed for successful implementation in high frequency applications.
Erratum: High‐frequency characterization of thin‐film Y‐Ba‐Cu oxide superconducting transmission lines [Appl. Phys. Lett. 52, 1444 (1988)]