Effect of tempering treatment on pitting corrosion resistance of modified cast CA6NM stainless steel in 3.5 % NaCl solution

2021 ◽  
Author(s):  
Vinda Puspasari ◽  
Mukhlis Agung Prasetyo ◽  
Arini Nikitasari ◽  
Efendi Mabruri ◽  
Moch. Syaiful Anwar
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
Pitting Corrosion ◽  
Nacl Solution ◽  
Pitting Corrosion Resistance ◽  
Tempering Treatment

NIROSTA 4429

Alloy Digest ◽  
2000 ◽  
Vol 49 (5) ◽  
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
High Temperature ◽  
Pitting Corrosion ◽  
Intergranular Corrosion ◽  
Heat Treating ◽  
Low Carbon ◽  
High Nitrogen ◽  
Temperature Performance ◽  
Pitting Corrosion Resistance

Abstract Nirosta 4429 is a low-carbon, high-nitrogen version of type 316 stainless steel. The low carbon imparts intergranular corrosion resistance while the nitrogen imparts both higher strength and some increased pitting corrosion resistance. It is recommended for use as welded parts that need not or cannot be annealed after welding. This datasheet provides information on composition, physical properties, elasticity, and tensile properties. It also includes information on high temperature performance and corrosion resistance as well as forming, heat treating, and joining. Filing Code: SS-787. Producer or source: ThyssenKrupp Nirosta.

Influence of Sigma Phase Precipitation on Pitting Corrosion of 2507 Super-Duplex Stainless Steel

2010 ◽  
Vol 658 ◽  
pp. 380-383 ◽  
Author(s):  
Ying Han ◽  
De Ning Zou ◽  
Wei Zhang ◽  
Jun Hui Yu ◽  
Yuan Yuan Qiao
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
Ambient Temperature ◽  
Duplex Stainless Steel ◽  
Pitting Corrosion ◽  
Super Duplex Stainless Steel ◽  
Phase Precipitation ◽  
Pitting Potential ◽  
Σ Phase ◽  
Pitting Corrosion Resistance

Specimens of 2507 super-duplex stainless steel aging at 850°C for 5 min, 15 min and 60 min were investigated to evaluate the pitting corrosion resistance in 3.5% NaCl solution at 30°C and 50°C. The results are correlated with the microstructures obtained with different aging time. The precipitation of σ phase remarkably decreases the pitting corrosion resistance of the steel and the specimen aged for 60 min presents the lowest pitting potential at both 30°C and 50°C. With increasing the ambient temperature from 30°C to 50°C, the pitting potential exhibits a reduction tendency, while this tendency is less obviously in enhancing the ambient temperature than in extending the isothermal aging duration from 5 to 60 min. SEM analysis shows that the surrounding regions of σ phase are the preferable sites for the formation of corrosion pits which grew up subsequently. This may be attributed to the lower content of corrosion resistance elements in these regions formatted with σ phase precipitation.

scholarly journals Pitting Corrosion Resistance on Annealing Treated Super Duplex Stainless Steel S32750

Crystals ◽  
2020 ◽  
Vol 10 (4) ◽  
pp. 294
Author(s):  
Shuang Liu ◽  
Chaohua Yue ◽  
Xi Chen ◽  
Qiuhua Zhu ◽  
Yiyou Tu
Keyword(s):  
Stainless Steel ◽  
Corrosion Resistance ◽  
Duplex Stainless Steel ◽  
Pitting Corrosion ◽  
Annealing Temperature ◽  
Super Duplex Stainless Steel ◽  
Boundary Area ◽  
Pitting Potential ◽  
Pitting Corrosion Resistance ◽  
Equivalent Number

The pitting corrosion resistance of S32750 super duplex stainless steel, annealing treated at temperatures of 950–1200 °C for 20–60 min, was investigated using potentiodynamic polarization tests. The results show that the volume fractions of ferrite in the S32750 duplex stainless steel increased from 48.9% to 68.4% as annealing temperatures increased from 950 to 1200 °C. The pitting potential of the sample increased first and then decreased from an annealing temperature of 950 to 1050 °C, and the highest pitting potential was observed after annealing at 1050 °C for 35 min. The pitting corrosion resistance of S32750 stainless steel is due to the combination of pitting resistance equivalent number (PREN) value, phase fraction and grain boundary area fraction, and the imbalance of corrosion potential.