An anhydrous orthophosphate, K3Eu5(PO4)6 (tripotassium pentaeuropium hexaphosphate), has been prepared by a high-temperature solid-state reaction combined with hydrothermal synthesis, and its crystal structure was determined by single-crystal X-ray diffraction analysis (SC-XRD). The results show that the compound crystallizes in the monoclinic space group C2/c and the structure features a three-dimensional framework of [Eu5(PO4)6]∞, with the tunnel filled by K+ ions. The IR spectrum, UV–Vis spectrum and luminescence properties of polycrystalline samples of K3Eu5(PO4)6, annealed at temperatures of 650, 700, 750, 800 and 850 °C, were investigated. Although with a full Eu3+ concentration (9.96 × 1021 ions cm−3), the self-activated phosphor K3Eu5(PO4)6 shows s strong luminescence emission intensity with a quantum yield of 37%. Under near-UV light excitation (393 nm), the series of samples shows the characteristic emissions of Eu3+ ions in the visible region from 575 to 715 nm. The sample sintered at 800 °C gives the strongest emission and its lifetime sintered at 800 °C (1.88 ms) is also the longest of all.
Hydrothermal synthesis and vacuum ultraviolet excited photoluminescence properties of (Y, La)VO4:Eu3+phosphors