401 Forming of recycled aluminum alloy sheet cast by a high speed twin roll caster

2013 ◽  
Vol 2013.21 (0) ◽  
pp. _401-1_-_401-5_
Author(s):  
Toshio HAGA
Keyword(s):  
Aluminum Alloy ◽  
High Speed ◽  
Alloy Sheet ◽  
Aluminum Alloy Sheet ◽  
Twin Roll Caster ◽  
Twin Roll

Inline Rolling of 5182 Aluminum Alloy Strip Cast by a Vertical Type High Speed Twin Roll Caster

2010 ◽  
Vol 139-141 ◽  
pp. 477-480
Author(s):  
Ryoji Nakamura ◽  
Shuya Hanada ◽  
Shinji Kumai ◽  
Hisaki Watari
Keyword(s):  
Aluminum Alloy ◽  
High Speed ◽  
Rolling Speed ◽  
Center Line ◽  
Alloy Strip ◽  
Ripple Mark ◽  
Roll Casting ◽  
Strip Cast ◽  
Twin Roll Caster ◽  
Twin Roll

An inline hot rolling was operated on 5182 aluminum alloy strip cast using a vertical type high speed caster (VHSTRC) at the speed of 60 m/min. A porosity existing at center line of the thickness and a ripple mark on the surface, these are typical defects of the strip cast by the VHSTRC, could be improved by the inline rolling. The rolling speed was as same as the roll-casting-speed of 60m/min. The temperature of the strip, when the inline rolling was operated, was 450oC. The reduction of the strip of the inline rolling was 35%.

Forming of Small Projection on Roll-Cast A356 Strip by Cold Rolling and Small Groove on PET Plate Using A356 Die

2019 ◽  
Vol 805 ◽  
pp. 37-42
Author(s):  
Toshio Haga ◽  
Yhuta Nakazawa
Keyword(s):  
Aluminum Alloy ◽  
Cold Rolling ◽  
Polyethylene Terephthalate ◽  
Alloy Sheet ◽  
Rolling Speed ◽  
A356 Aluminum Alloy ◽  
Aluminum Alloy Sheet ◽  
A356 Aluminum ◽  
Twin Roll Cast ◽  
Twin Roll

A small projection with a height and width of about 40 and 50 µm, respectively, was formed on a twin-roll-cast A356 aluminum alloy sheet by cold rolling at a rolling speed of 0.5 m/min. This projection was then used as a die to form a groove with a depth and width of about 40 and 50 µm, respectively, on a polyethylene terephthalate plate by pressing.

High Speed Twin-Roll Casting of Al-Mg Alloys

2010 ◽  
Vol 154-155 ◽  
pp. 1544-1548 ◽  
Author(s):  
Kosuke Komeda ◽  
Ryoji Nakamura ◽  
Shinji Kumai
Keyword(s):  
Heat Transfer ◽  
Aluminum Alloy ◽  
High Speed ◽  
Aluminum Alloy 5182 ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Deep Drawing Test ◽  
Study Heat Transfer ◽  
Twin Roll ◽  
Steel Rolls

The disadvantages of the conventional twin-roll caster for aluminum alloy are low casting speeds and limited choices of alloys that are castable by this processing. It is known that strip casting of aluminum alloy 5182 is very difficult because of their wider freezing zones. The vertical-type high-speed twin-roll caster used in the present study was devised to overcome these disadvantages. Features of the high speed twin roll casters are as below. Mild steel rolls were used in order to increase the casting speed and to be made at a lower equipment cost. Roll coating is produced in casting of Al-Mg alloy. Therefore lubricant, that resists heat transfer, was not used in the present study. Heat transfer between melt and the roll was improved by hydrostatic pressure of the melt. Low superheat casting was carried out in order to improve microstructure of the strip. In the present study, effectiveness of a high-speed twin roll caster for recycling aluminum alloy was investigated. The effects of the high-speed twin roll caster on alleviating the deterioration of mechanical properties by impurities were investigated. Properties of the cast strip were investigated by metalography, a tension test, and a deep drawing test.

scholarly journals Effect of Cooling Rate on Microstructure and Properties of Twin-Roll Casting 6061 Aluminum Alloy Sheet

Metals ◽  
2020 ◽  
Vol 10 (9) ◽  
pp. 1168 ◽  
Author(s):  
Zhen Xu ◽  
Sixue Wang ◽  
Hongbin Wang ◽  
Hua Song ◽  
Shengli Li ◽  
...  
Keyword(s):  
Grain Size ◽  
Aluminum Alloy ◽  
Cooling Rate ◽  
Alloy Sheet ◽  
Aluminum Alloy Sheet ◽  
6061 Aluminum Alloy ◽  
Microstructure And Properties ◽  
Twin Roll Casting ◽  
Roll Casting ◽  
Twin Roll

In this study, a twin-roll casting sheet of 6061 aluminum alloy was cooled using furnace, asbestos, air, wind and water. The effect of cooling rate on the microstructure and properties of twin-roll casting 6061 aluminum alloy sheet were studied. Optical microscope, scanning electron microscope, X-ray diffraction, microhardness tester and universal tensile machine were used to observe the microstructure and properties of twin-roll casting sheet of 6061 aluminum alloy. The results show that the higher the cooling rate, the smaller the grain size of the alloy and the smaller the number of precipitated phases in the matrix. Uniform grain size of the alloy could be obtained at a stable cooling rate. The hardness, tensile strength and elongation of the twin-roll casting sheet increased with cooling rate. Under wind cooling condition, the twin-roll casting sheet demonstrated excellent comprehensive performance, i.e., 88 MPa of yield strength, 178 MPa of tensile strength and 15% of elongation, respectively. A quantitative Hall–Petch relation was established to predict the yield strength of 6061 twin-roll casting sheets with different grain sizes and cooling rate.

scholarly journals Effect of Roll Surface on Aluminum Alloy Strip Fabricated by a High-Speed Twin Roll Caster

2013 ◽  
Vol 79 (804) ◽  
pp. 1156-1160
Author(s):  
Takuya YAMASHIKI ◽  
Toshio HAGA ◽  
Shinji KUMAI ◽  
Hisaki WATARI
Keyword(s):  
Aluminum Alloy ◽  
High Speed ◽  
Alloy Strip ◽  
Roll Surface ◽  
Twin Roll Caster ◽  
Twin Roll

scholarly journals Effect of Side-Dam Plate on Burrs at Edges of Aluminum Alloy Strip Fabricated by a High Speed Twin Roll Caster

2013 ◽  
Vol 79 (804) ◽  
pp. 1152-1155
Author(s):  
Takuya YAMASHIKI ◽  
Yuki SHIRAKAWA ◽  
Toshio HAGA ◽  
Shinji KUMAI ◽  
Hisaki WATARI
Keyword(s):  
Aluminum Alloy ◽  
High Speed ◽  
Alloy Strip ◽  
Twin Roll Caster ◽  
Twin Roll

scholarly journals High Speed Roll Caster for Aluminum Alloy

Metals ◽  
2021 ◽  
Vol 11 (3) ◽  
pp. 520
Author(s):  
Toshio Haga
Keyword(s):  
Thermal Conductivity ◽  
Aluminum Alloy ◽  
Copper Alloy ◽  
High Speed ◽  
The Other ◽  
Center Line ◽  
Cast Strip ◽  
Roll Casting ◽  
Twin Roll Caster ◽  
Twin Roll

Two types of high-speed twin-roll casters and a single-roll caster equipped with a scraper were proposed. One of the twin-roll casters is a vertical-type high-speed twin-roll caster, and the other twin-roll caster is an unequal-diameter twin-roll caster. The vertical-type high-speed twin-roll caster can cast strip at speeds of up to 120 m/min. The unequal-diameter twin-roll caster casts strip at speeds up to 60 m/min. The unequal-diameter twin-roll caster is superior to the vertical-type high-speed twin-roll caster at the point of conveyance of the cast strip. A single-roll caster equipped with a scraper can cast strip without center-line segregation at speeds of up to 40 m/min. The use of a copper alloy roll and the non-use of a parting material enable high-speed roll casting. Since the roll loads of these casters are smaller than 0.1 kN/mm, soft copper alloy roll can be used. The strip does not stick to the roll without the parting material because of the use of the copper alloy roll with high thermal conductivity and the small roll load. The cooling rate near the surface is higher than 2000 °C/s.