Effect of surface treatment conditions of zirconia on the shear bond strength of orthodontic metal bracket

These days, new prosthodontic materials are appearing with the development of digitalization. Among these, the use of polyetheretherketone (PEEK) as the clasp of removable partial dentures has been proposed. The adhesive strength between the PEEK and acrylic resin influences the probability of denture fracture. To investigate the effect of PEEK surface treatments on the shear bond strength to acrylic resin, five surface treatment conditions of PEEK were analyzed: 1. no treatment; 2. ceramic primer application; 3. Al2O3 sandblasting; 4. Rocatec; and 5. Rocatec with ceramic primer application, comparing with a metal primer-treated Co-Cr alloy. Two kinds of autopolymerizing resin (Unifast II and Palapress Vario) were used as bonding materials. The specimens were evaluated to determine the bond strength. Rocatec treatment with ceramic primer application yielded the highest bond strengths (12.71 MPa and 15.32 MPa, respectively, for Unifast II and Palapress Vario). When compared to a metal primer-treated Co-Cr alloy, the bond strength of PEEK to Unifast II was similar, whereas it was about 60% of that to Palapress Vario. Rocatec treatment, combined with ceramic primer, showed the highest bond strength of PEEK to acrylic resin. Treatment of PEEK will enable its use as the clasp of removable dentures and the fixation of PEEK prostheses.

Download Full-text

Effect of Surface Treatment and Storage Time on Immediate Repair Bond Strength Durability of Methacrylate- and Ormocer-Based Bulk Fill Resin Composites

Applied Sciences ◽

10.3390/app10228308 ◽

2020 ◽

Vol 10 (22) ◽

pp. 8308

Author(s):

Farid S. El-Askary ◽

Sara A. Botros ◽

Mutlu Özcan

Keyword(s):

Bond Strength ◽

Surface Treatment ◽

Shear Bond Strength ◽

Storage Time ◽

Strength Testing ◽

Repair System ◽

Resin Composites ◽

Oxygen Inhibition ◽

And Storage ◽

Effect Of Surface

The aim of this study was to evaluate the effect of surface treatment and storage time on immediate repair bond durability of methacrylate- and ormocer-based bulk fill composites. In total, 265 discs were divided into 32 groups (n = 8/group) according to: (1) Material: X-tra fil and Admira Fusion X-tra; (2) Surface treatment: oxygen inhibition; matrix; Futurabond M+; Silane/Futurabond M+; Admira Bond; Silane/Admira Bond; ceramic repair system; and Silane/Cimara bond; and (3) Storage time: 24 h and 6 months. Each disc received three micro-cylinders from the same material. Specimens were subjected to micro-shear bond strength testing either at 24 h or 6 months. Data were analyzed using ANOVA/Tukey’s test/Student t-test (p = 0.05). All experimental factors had significant effect on bond strength (p < 0.0001). Drop in bond strength was noticed in both materials after six months (p < 0.05), except for Admira Fusion X-tra treated with silane/cimara adhesive (p = 0.860). Both materials showed insignificant values with Admira bond either at 24 h or 6 months (p = 0.275 and p = 0.060, respectively). For other treatments, X-tra fil showed significantly higher values at 24 h and 6 months (p < 0.05). Ceramic repair system can be used to immediately repair both methacrylate- and ormocer-based composites.