Mechanical Properties of Carbon Fiber Reinforced Nanocrystalline Nickel Composite Electroforming Deposit
AbstractIn order to obtain higher strength fiber reinforced composite electroforming deposit, carbon fiber reinforced nanocrystalline nickel composite electroforming deposit was prepared by electrodepositing with pulse current and a flexible wheel was applied to rub and extrude the electroforming deposit. Results shown that when the grains of the carbon fiber reinforced nickel composite electroforming deposit were refined from micron to 80nm at room temperature, the microhardness increased from 230Hv to 740Hv, and the tensile strength increased from 1025MPa to 1472MPa. With the further refinement of the grains of the electroforming deposit, the tensile strength decreased significantly due to the decrease of the bonding strength between the carbon fiber and the nickel matrix, while the microhardness still increased to 758Hv. At 200°C, the carbon fiber reinforced nanocrystalline nickel composite electroforming deposit still showed high strength. When the temperature rose to 400°C, the influence of nanocrystalline on the tensile strength of the carbon fiber reinforced nickel composite electroforming deposit was no longer significant, due to the rapid growth of crystal grains and the precipitation of interfacial brittle substances.